The long-term degradation of epoxy as the matrix and adhesive serviced in harsh environments plays a key role in engineering applications. Understanding how to improve the toughness and durability of epoxy through reasonable material replacement and design is significant to prolong the service life of engineering structures. In the present paper, thermoplastic polypropylene and thermosetting epoxy were exposed in a coupling environment of elevated temperature, water immersion and sustained bending loading. The evolutions of mechanical and thermal properties were further analyzed and compared. Long-term life prediction was conducted to evaluate the corrosive resistances of polypropylene and epoxy. It can be found that polypropylene has better hydrophobic behavior compared to epoxy. At 80 °C, the ratios of the diffusion coefficient and saturated water uptake between the two matrices were 114.4 and 2.94. At the longest immersion time of 90 days, the degradation percentages of tensile strength were 4.7% (40 °C), 7.5% (60 °C) and 8.8% (80 °C), respectively, which had the higher strength retention (>90%). The maximum strength increase in the multiples of polypropylene/epoxy and polypropylene/polyurethane was 1.95 and 1.75, respectively. The bending loading led to a maximum increase in tensile strength (~1.47%) owing to the oxygen isolation effect. The degradation mechanism was attributed to the active functional groups from the production process reacting with oxygen, resulting in the fracture of the local chain segment. By comparison, water molecules reacted with the hydroxyl groups or interrupted the intermolecular Van der Waals force/hydrogen bond of the epoxy, resulting in irreversible hydrolysis and property degradation. Through the comparison, it can be found that polypropylene and its composites have outstanding properties compared to epoxy, which can make them achieve great application prospects in engineering applications when considering a complex service environment.

Processing parameters play a key role in the mechanical, thermo-mechanical and creep-recovery properties of unidirectional carbon fiber reinforced thermoplastic polypropylene (CF/PP) composites because of high matrix viscosity, which governs their impregnation and interfacial bonding. This study systematically investigates the effects of molding temperature (190~210 °C), pressure (1~3 MPa), and holding time (5~15 min) on its short beam strength (SBS), storage modulus, loss modulus, tan δ, creep strain, strain recovery, and crystallinity using a Taguchi experimental design. The results presented that processing parameters have a huge effect on CF/PP composites’ SBS, and through the experimental design, the SBS could be improved by 68.1% (21.3~35.8 MPa). Holding time is the most influential parameter for SBS and damping performance, while temperature and pressure interact strongly, highlighting the importance of parameter synergy. There was a strong negative correlation between the crystallinity degree and the SBS of CF/PP composites, and a higher crystallinity degree means a sharper and higher melting peak. Creep-recovery tests reveal near-complete recovery (87~102%) at 30 °C, which decreases to 71~79% at 80 °C due to increased matrix mobility. Finally, it was confirmed that the relatively low SBS of CF/PP composites comes from the void and incomplete matrix impregnation of fibers. The above results advance the design of high-performance, sustainable thermoplastic composites for civil and structural engineering applications.