Bone marrow is an important source of stem cells, which can promote bone fracture healing. We investigated the optimal time to inject bone marrow mesenchymal stem cells (BMSCs) in a C57 murine unilateral, transverse, femur fracture model. BMSCs transfected with red fluorescent protein (RFP-BMSCs) were injected via the tail vein on day 1, 7, or 14 post-fracture. AMD3100 (inhibitor of stromal cell-derived factor 1 [SDF-1]) was also injected before RFP-BMSCs in one group for comparison; a control group received saline injections. RFP-BMSC migration and fracture healing were evaluated by in vivo fluorescence assay. Micro-CT was performed and mechanical testing and histological analysis. Chemokine levels were evaluated by quantitative real-time PCR and western blotting. Following injection on day 7 post-fracture, RFP-BMSCs more frequently homed to the fracture site and remained for a longer duration. Bone volume and bone mineral density were increased when BMSCs were injected on day 7 post-fracture (P < 0.05). The mechanical properties of fractured femurs were improved following day-7 BMSC injection. Histology confirmed that BMSC injection improved the formation of new bones. Chemokines that induce BMSC migration were highly expressed, and protein levels of osteogenesis-related factors were increased. Seven days after fracture may be the optimal time for injection of BMSCs to promote fracture healing. Additionally, the SDF-1/CXCR4 pathway may play an important role in fracture healing following BMSC injection.

/Objective: The treatment of bone defect has always been a difficult problem in orthopedic clinic. The search for alternative biodegradable implants is a hot topic. The development of biodegradable magnesium scaffolds for the treatment of bone defects has long been a goal of the public. In this study, we proposed a porous magnesium scaffold prepared by 3D gel printing and surface modification with an additional calcium phosphate coating and use of its strength, degradability and slow degradation rate in a bone graft substitute material. The porous magnesium granular scaffold was prepared by 3D gel printing technology and modified by DCPD (Dibasic Calcium Phosphate Dihydrate) coating. The biocompatibility, degradation rate, and osteogenic ability of the scaffold were evaluated in vitro and in vivo. The biocompatibility, in vivo degradation and bone defect healing response of the implants were investigated. Porous magnesium scaffolds were successfully prepared, and the strength of sintered scaffolds reached 5.38 ​MPa. The degradation rates of scaffolds were significantly reduced after coating with DCPD. The cell compatibility evaluation showed that DCPD-coated Mg scaffold was suitable for cell proliferation. In vivo biosafety monitoring showed that scaffold implantation did not cause an increase in Mg ion concentration in vivo, and no toxic damage was detected in the liver or kidney. Micro-CT and pathological results showed that a large amount of new bone was formed at 6 weeks. At 12 weeks, approximately 52% of the scaffold volume remained. At 24 weeks, osteogenesis, which was stimulated by some residual scaffold, still can be observed. In summary, this study suggests that 3D gel-printed DCPD-coated porous magnesium scaffolds have great potential as bone graft alternatives. In summary, this study suggests that 3D gel-printed DCPD-coated porous magnesium scaffolds have great potential as bone graft alternatives. The translational potential of this article is to make use of the advantages of 3D gel printing technology with higher efficiency and lower cost compared with SLM and SLS technologies, and use pure magnesium powder as raw material to prepare degradable porous magnesium metal scaffolds, opening up a new technical route for the preparation of degradable porous magnesium scaffolds which are made for bone defect regeneration in the future.

Autologous nerve grafting serves is considered the gold standard treatment for peripheral nerve defects; however, limited availability and donor area destruction restrict its widespread clinical application. Although the performance of allogeneic decellularized nerve implants has been explored, challenges such as insufficient human donors have been a major drawback to its clinical use. Tissue-engineered neural regeneration materials have been developed over the years, and researchers have explored strategies to mimic the peripheral neural microenvironment during the design of nerve catheter grafts, namely the extracellular matrix (ECM), which includes mechanical, physical, and biochemical signals that support nerve regeneration. In this study, polycaprolactone/silk fibroin (PCL/SF)-aligned electrospun material was modified with ECM derived from human umbilical cord mesenchymal stem cells (hUMSCs), and a dual-bionic nerve regeneration material was successfully fabricated. The results indicated that the developed biomimetic material had excellent biological properties, providing sufficient anchorage for Schwann cells and subsequent axon regeneration and angiogenesis processes. Moreover, the dual-bionic material exerted a similar effect to that of autologous nerve transplantation in bridging peripheral nerve defects in rats. In conclusion, this study provides a new concept for designing neural regeneration materials, and the prepared dual-bionic repair materials have excellent auxiliary regenerative ability and further preclinical testing is warranted to evaluate its clinical application potential.

To prepare adipose-derived stem cells (ADSCs)-embedded alginate-gelatinemicrospheres (Alg-Gel-ADSCs MSs) by electrospray and evaluate their feasibility for cartilage tissue engineering. To observe the efficacy of Alg-Gel-ADSCs MSs in repairing articular cartilage defects in SD rats. ADSCs were isolated and characterized by performing induced differentiation and flow cytometry assays. Alginate-gelatine microspheres with different gelatine concentrations were manufactured by electrospraying, and the appropriate alginate-gelatine concentration and ratio were determined by evaluating microsphere formation. Alg-Gel-ADSCs MSs were compared with Alg-ADSCs MSs through the induction of chondrogenic differentiation and culture. Their feasibility for cartilage tissue engineering was analysed by performing Live/Dead staining, cell proliferation analysis, toluidine blue staining and a glycosaminoglycan (GAG) content analysis. Alg-Gel-ADSCs MSs were implanted in the cartilage defects of SD rats, and the cartilage repair effect was evaluated at different time points. The evaluation included gross observations and histological evaluations, fluorescence imaging tracking, immunohistochemical staining, microcomputed tomography (micro-CT) and a CatWalk evaluation. The isolated ADSCs showed multidirectional differentiation and were used for cartilage tissue engineering. Using 1.5 w:v% alginate and 0.5 w:v% gelatine (Type B), we successfully prepared nearly spherical microspheres. Compared with alginate microspheres, alginate gel increased the viability of ADSCs and promoted the proliferation and chondrogenesis of ADSCs. In our experiments on knee cartilage defects in SD rats in vivo, the Alg-Gel-ADSCs MSs showed superior cartilage repair in cell resides, histology evaluation, micro-CT imaging and gait analysis. Microspheres composed of 1.5 w:v% alginate-0.5 w:v% gelatine increase the viability of ADSCs and supported their proliferation and deposition of cartilage matrix components. ADSCs embedded in 1.5 w:v% alginate-0.5 w:v% gelatine microspheres show superior repair efficacy and prospective applications in cartilage tissue repair. In this study, injectable adipose-derived stem cells-embedded alginate-gelatin microspheres (Alg-Gel-ADSCs MSs) were prepared by the electrospray . Compared with the traditional alginate microspheres, its support ability for ADSCs is better and shows a better repair effect. This study provides a promising strategy for cartilage tissue regeneration.

Osteochondral interface regeneration is challenging for functional and integrated cartilage repair. Various layered scaffolds have been used to reconstruct the complex interface, yet the influence of the permeability of the layered structure on cartilage defect healing remains largely unknown. We designed and fabricated a novel bilayered scaffold using articular cartilage extracellular matrix (ACECM) and hydroxyapatite (HAp), involving a porous, oriented upper layer and a dense, mineralised lower layer. By optimising the HAp/ACECM ratio, differing pore sizes and porosities were obtained simultaneously in the two layers. To evaluate the effects of permeability on cell behaviour, rabbit chondrocytes were seeded. Morphological observations demonstrated that a gradual interfacial region was formed with pore sizes varying from 128.2 ± 20.3 to 21.2 ± 3.1 μm. The permeability of the bilayered scaffold decreased with increasing compressive strain and HAp content. Mechanical tests indicated that the interface was stable to bearing compressive and shear loads. Accordingly, the optimum HAp/ACECM ratio (7 w/v%) in the layer to mimic native calcified cartilage was found. Chondrocytes could not penetrate the interface and resided only in the upper layer, where they showed high cellularity and abundant matrix deposition. Our findings suggest that a bilayered scaffold with low permeability, rather than complete isolation, represents a promising candidate for osteochondral interface tissue engineering.