The current work concentrated on the green synthesis of silver nanoparticles (AgNPs) through the use of aqueous Citruslimon zest extract, optimizing the different experimental factors required for the formation and stability of AgNPs. The preparation of nanoparticles was confirmed by the observation of the color change of the mixture of silver nitrate, after the addition of the plant extract, from yellow to a reddish-brown colloidal suspension and was established by detecting the surface plasmon resonance band at 535.5 nm, utilizing UV-Visible analysis. The optimum conditions were found to be 1 mM of silver nitrate concentration, a 1:9 ratio extract of the mixture, and a 4 h incubation period. Fourier transform infrared spectroscopy spectrum indicated that the phytochemicals compounds present in Citrus limon zest extract had a fundamental effect on the production of AgNPs as a bio-reducing agent. The morphology, size, and elemental composition of AgNPs were investigated by zeta potential (ZP), dynamic light scattering (DLS), SEM, EDX, X-ray diffraction (XRD), and transmission electron microscopy (TEM) analysis, which showed crystalline spherical silver nanoparticles. In addition, the antimicrobial and antioxidant properties of this bioactive silver nanoparticle were also investigated. The AgNPs showed excellent antibacterial activity against one Gram-negative pathogens bacteria, Escherichia coli, and one Gram-positive bacteria, Staphylococcus aureus, as well as antifungal activity against Candida albicans. The obtained results indicate that the antioxidant activity of this nanoparticle is significant. This bioactive silver nanoparticle can be used in biomedical and pharmacological fields.

The treatment of aviation industry metal plating wastewater containing Ni²⁺ and Cr⁶⁺ by nanofiltration was investigated in this study. Two commercial membranes (NF90 and NF270) and two membrane filtration systems (dead end and cross flow) were used. The effects of both the transmembrane pressure (10, 20, and 30 bar) and the feed pH (3.5, 7, and 10) on the membrane performance were analyzed. The rejection of both nickel and chromium ions increased with increasing pH but did not considerably change by the pressure difference for both membranes. The optimum conditions were found to be at 30 bar with a pH of 10 for both the NF90 and NF270 membranes. Under optimum conditions for the NF90 membrane, the rejection values of Ni²⁺ and Cr⁶⁺ were found to be 99.2 and 96.5%, respectively. For the NF270 membrane, the rejection values of Ni²⁺ and Cr⁶⁺ were 98.7 and 95.7%, respectively.

In this study, the degradation of azo dye solutions (Reactive Red 180 and Reactive Orange 16) of textile industry wastewater was investigated for using innovative hybrid process of photocatalytic and membrane distillation (MD) processes. Photocatalytic oxidation was conducted with semiconductor catalysts (ZnO and TiO2) and their mixture under UVA and UVC irradiation. More effective results were obtained under UVA at the initial stages of the reactions for both dye solutions. ZnO and TiO2 catalysts have given similar efficient results, but results with ZnO were better at initial stages. For the next stage, hybrid design of MD and photocatalytic processes was performed sequentially. Initially, the photocatalytic process was conducted for at least 1 h at initial values of 100 mg/L RR-180 dye solutions and 1 g/L ZnO catalyst loading under UVA irradiation and then treated solution was run through the distillation module at different temperatures (30°C and 40°C) and flow rates (210, 425, and 665 mL/min). Three types of membranes (polypropylene, polytetrafluoroethylene, and polyvinylidene fluoride) with different pore sizes (0.45 and 0.22 μm) were used in the module. Increasing temperature on the side of treated solution and decreasing the temperature on the other side has increased the distillate efficiency.

Food processing industry by-products (apple, pomegranate, black carrot, and red beet pulps) were evaluated as raw materials in pigment production by the filamentous fungi Aspergillus carbonarius. The effect of fermentation conditions (solid and submerged-state), incubation period (3, 6, 9, 12, and 15 d), initial substrate pH (4.5, 5.5, 6.5, 7.5, and 8.5), and pulp particle size (4 mm) on fungal pigment production were tested to optimize the conditions. Pigment extraction analysis carried out under solid-state fermentation conditions showed that the maximum pigment production was determined as 9.21 ± 0.59 absorbance unit at the corresponding wavelength per gram (AU/g) dry fermented mass (dfm) for pomegranate pulp (PP) by A. carbonarius for 5 d. Moreover, the highest pigment production was obtained as 61.84 ± 2.16 AU/g dfm as yellowish brown at initial pH 6.5 with < 1.4 mm of substrate particle size for 15-d incubation period. GC×GC-TOFMS results indicate that melanin could be one of the main products as a pigment. SEM images showed that melanin could localize on the conidia of A. carbonarius.