Commercial wearable piezoelectric sensors possess excellent anti-interference stability due to their electronic packaging. However, this packaging renders them barely breathable and compromises human comfort. To address this issue, we develop a PVDF piezoelectric nanoyarns with an ultrahigh strength of 313.3 MPa, weaving them with different yarns to form three-dimensional piezoelectric fabric (3DPF) sensor using the advanced 3D textile technology. The tensile strength (46.0 MPa) of 3DPF exhibits the highest among the reported flexible piezoelectric sensors. The 3DPF features anti-gravity unidirectional liquid transport that allows sweat to move from the inner layer near to the skin to the outer layer in 4 s, resulting in a comfortable and dry environment for the user. It should be noted that sweating does not weaken the piezoelectric properties of 3DPF, but rather enhances. Additionally, the durability and comfortability of 3DPF are similar to those of the commercial cotton T-shirts. This work provides a strategy for developing comfortable flexible wearable electronic devices.

Body temperature is an important indicator of human health. The traditional mercury and medical electronic thermometers have a slow response (≥1 min) and can not be worn for long to achieve continuous temperature monitoring due to their rigidity. In this work, we prepared a skin-core structure polyurethane (PU)/graphene encapsulated poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) temperature-sensitive fiber in one step by combining wet spinning technology with impregnation technology. The composite fiber has high sensitivity (-1.72%/°C), super-resolution (0.1 °C), fast time response (17 s), antisweat interference, and high linearity (R² = 0.98) in the temperature sensing range of 30-50 °C. The fiber is strong enough to be braided into the temperature-sensitive fabric with commercial cotton yarns. The fabric with good comfort and durability can be arranged in the armpit position of the cloth to realize real-time body temperature monitoring without interruption during daily activities. Through Bluetooth wireless transmission, body temperature can be monitored in real-time and displayed on mobile phones to the parents or guardians. Overall, the fiber-based temperature sensor will significantly improve the practical applications of wearable temperature sensors in intelligent medical treatment due to its sensing stability, comfort, and durability.

MXene, a transition metal carbide/nitride, has been prominent as an ideal electrochemical active material for supercapacitors. However, the low MXene load limits its practical applications. As environmental concerns and sustainable development become more widely recognized, it is necessary to explore a greener and cleaner technology to recycle textile by-products such as cotton. The present study proposes an effective 3D fabrication method that uses MXene to fabricate waste denim felt into ultralight and flexible supercapacitors through needling and carbonization. The 3D structure provided more sites for loading MXene onto Z-directional fiber bundles, resulting in more efficient ion exchange between the electrolyte and electrodes. Furthermore, the carbonization process removed the specific adverse groups in MXenes, further improving the specific capacitance, energy density, power density and electrical conductivity of supercapacitors. The electrodes achieve a maximum specific capacitance of 1748.5 mF cm⁻² and demonstrate remarkable cycling stability maintaining more than 94% after 15,000 galvanostatic charge/discharge cycles. Besides, the obtained supercapacitors present a maximum specific capacitance of 577.5 mF cm⁻², energy density of 80.2 μWh cm⁻² and power density of 3 mW cm⁻², respectively. The resulting supercapacitors can be used to develop smart wearable power devices such as smartwatches, laying the foundation for a novel strategy of utilizing waste cotton in a high-quality manner.