To improve sustainability of polymers and to reduce carbon footprint, polymers from renewable resources are given significant attention due to the developing concern over environmental protection. The renewable materials are progressively used in many technical applications instead of short-term-use products. However, among other applications, the flame retardancy of such polymers needs to be improved for technical applications due to potential fire risk and their involvement in our daily life. To overcome this potential risk, various flame retardants (FRs) compounds based on conventional and non-conventional approaches such as inorganic FRs, nitrogen-based FRs, halogenated FRs and nanofillers were synthesized. However, most of the conventional FRs are non-biodegradable and if disposed in the landfill, microorganisms in the soil or water cannot degrade them. Hence, they remain in the environment for long time and may find their way not only in the food chain but can also easily attach to any airborne particle and can travel distances and may end up in freshwater, food products, ecosystems, or even can be inhaled if they are present in the air. Furthermore, it is not a good choice to use non-biodegradable FRs in biodegradable polymers such as polylactic acid (PLA). Therefore, the goal of this review paper is to promote the use of biodegradable and bio-based compounds for flame retardants used in polymeric materials.

Starch, being a polyhydric compound with its natural charring ability, is an ideal candidate to serve as a carbonization agent in an intumescent system. This charring ability of starch, if accompanied by an acidic source, can generate an effective intumescent flame retardant (IFR) system, but the performance of starch-based composites in an IFR system has not been tested in detail. Here, we describe a PLA-based IFR system consisting of ammonium polyphosphate (APP) as acidic source and cornstarch as carbon source. We prepared different formulations by melt compounding followed by molding into sheets by hot pressing. The thermal behavior and surface morphology of the composites was investigated by thermogravimetric analysis and scanning electron microscopy respectively. We also conducted limiting oxygen index (LOI), UL-94, and cone calorimetry tests to characterize the flame-retardant properties. Cone calorimetry revealed a 66% reduction in the peak heat release rate of the IFR composites compared to pure PLA and indicated the development of an intumescent structure by leaving a residual mass of 43% relative to the initial mass of the sample. A mechanism of char formation has also been discussed in detail.

Recycling the waste for environmental protection has been an important challenge for the mankind. The fibrous waste in textile industry accounts for approximately 15% of the amount of fibers used, leading to a lower yield %. The current study focused to use this waste as reinforcement to produce a fiber-reinforced polymer composites. Reinforcements were woven in 3/1 S twill, using yarn produced from noil waste and knitting waste in the weft direction. The weft yarn count, type of waste material and number of picks were the variables of study. Laminated composites were fabricated from these reinforcements and the mechanical properties (tensile, bending and impact) were compared to the conventional glass fiber composites. The specific mechanical properties of these composites were found comparable or less than that of glass fiber composites.

In this study, six different woven samples were produced on air jet loom with two different weave designs (i.e. 3/1 twill and 1/1 plain), three different picking sequences (i.e. single pick insertion (SPI), double pick insertion (DPI) and three pick insertion (3PI)). All the woven samples were singed, desized, bleached and finished together at industrial scale, as a single lot. The effect of these factors on the wetting, wicking and air permeability (AP) of the fabric samples was analysed. It was revealed that the fabric weave design and picking sequence has statistically significant effect on fabric wetting time, water spreading speed and AP of the fabric. It was found that fabrics woven in twill weave design and with simultaneous 3PI give significantly better AP, shorter wetting time and better water spreading rate as compared to plain woven fabrics and those with double or SPI. It could be concluded that the thermophysiological comfort of woven fabrics may be significantly improved simply by selecting a suitable weave design and picking sequence.

Biodegradable polymers from renewable resources have attracted interest due to environmental pollution caused by the disposal of non-degradable polymers, and engineering them to produce fibres of textile grade can improve the environmental sustainability of textile sector. Flame retardancy of polylactic acid (PLA) can be improved if used in intumescent system containing acidic and carbonic source; however, spinning them to produce fibres of textile grade is a big challenge. We therefore have prepared PLA composites containing phosphorous–nitrogen-based flame retardant as acidic source together with kraft lignin as carbonic source. Different quantities of flame retardant and kraft lignin were added to PLA matrix by melt blending and then hot-pressed to form moulding sheets. A modified polyester-based plasticizer was also incorporated to facilitate the spinnability of the composites. Limiting oxygen index values and UL-94 ratings of the composites were reported. The melt spinnability of composites was then assessed, and flame retardancy of knitted structures produced from multifilament yarns was tested by cone calorimetry. Composites containing up to 7% (m/m) of lignin were spinnable together with 10% (m/m) of plasticizer. A substantial decrease of 59% in heat release rate was observed compared to pure PLA. The mechanism of intumescence was also reported.

The objective of this study is to assess the efficiency of biobased carbonization agent in intumescent formulations (IFRs) to examine the flame retardant properties of polylactic acid (PLA) composites and to investigate their melt-spinnability. We used phosphorous-based halogen free flame retardant (FR) and kraft lignin (KL) as bio-based carbonization agent. After melt compounding and molding into sheets by hot pressing various fire related characteristics of IFR composites were inspected and were characterized by different characterization methods. It was fascinating to discover that the introduction of 5–20 wt% FR increased the limiting oxygen index (LOI) of PLA composites from 20.1% to 23.2–33.5%. The addition of KL with content of 3–5 wt% further increased the LOI up to 36.6–37.8% and also endowed PLA/FR/KL composites with improved anti-dripping properties. Cone calorimetry revealed a 50% reduction in the peak heat release rate of the IFR composites in comparison to 100% PLA and confirmed the development of an intumescent char structure containing residue up to 40%. For comparative study, IFR composites containing pentaerythritol (PER) as a carbonization agent were also prepared and their FR properties were compared. IFR composites were melt spun and mechanical properties of multifilament yarns were tested. The analysis of char residues by energy dispersive X-ray spectrometry (EDS) and SEM images confirmed that PLA/FR/KL composites developed a thicker and more homogeneous char layer with better flame retardant properties confirming that the fire properties of PLA can be enhanced by using KL as a carbonization agent.