Functionally graded materials (FGMs) belong to a new, continuously developing group of materials, finding application in various branches of industry. The idea of freely designing their construction profile, restricted only by the available manufacturing techniques, enables obtaining materials with composition and structure gradients having unprecedented properties. In this paper, selected results of works carried out by the authors and relating to the application of the developed metal-ceramic composites were presented in order to manufacture functionally graded materials for target purposes. Gradient structures with various construction profiles that can play different roles were produced on the basis on the following material pairs: Cr-Al₂O₃, NiAl-Al₂O₃ and Cu-AlN. Manufacturing conditions, microstructure characteristics and selected properties, crucial from the point of view of future applications, were presented.

It is commonly known that the properties of sintered materials are strongly related to technological conditions of the densification process. This paper shows the sintering behavior of a NiAl-Al₂O₃ composite, and its individual components sintered separately. Each kind of material was processed via the powder metallurgy route (hot pressing). The progress of sintering at different stages of the process was tested. Changes in the microstructure were examined using scanning and transmission electron microscopy. Metal-ceramics interface was clean and no additional phases were detected. Correlation between the microstructure, density, and mechanical properties of the sintered materials was analyzed. The values of elastic constants of NiAl/Al₂O₃ were close to intermetallic ones due to the volume content of the NiAl phase particularly at low densities, where small alumina particles had no impact on the composite’s stiffness. The influence of the external pressure of 30 MPa seemed crucial for obtaining satisfactory stiffness for three kinds of the studied materials which were characterized by a high dense microstructure with a low number of isolated spherical pores.

The paper presents the results of research on the production by means of arc spraying of composite coatings from the Fe-Al system with participation of in-situ intermetallic phases. The arc spraying process was carried out by simultaneously melting two different electrode wires, aluminum and steel. The aim of the research is to create protective coatings with a composite structure with a significant participation of Fe_xAl_y as an intermetallic phases reinforcement. The synthesis of intermetallic phases takes place during the (in-situ) spraying process. Currently most coatings involving intermetallic phases are manufactured by different thermal spraying methods using coating materials in the form of prefabricated powders containing intermetallic phases. The obtained results showed the local occurrence of intermetallic phases from the Fe-Al system, and the dominant components of the structure have two phases, aluminum solid solutions in iron and iron in aluminum. The participation of intermetallic phases in the coating is relatively low, but its effect on the properties of the coating material is significant.

The influence of hot pressing conditions on mechanical properties of nickel aluminide/alumina composite has been investigated in the present paper. In particular, effect of the process parameters, viz. compacting pressure, sintering temperature and sintering time on the evolution of density, elastic constants and tensile strength properties of the intermetallic-ceramic composite has been studied. Elastic constants, the Young's modulus and Poisson's ratio, have been evaluated using an ultrasonic testing method, and the tensile strength has been determined by a Brazilian-type splitting test. Microscopic observations of microstructure evolution complemented the experimental procedure. Experimental results have been confronted with theoretical models showing a good agreement between the data compared.