Objectives:This study investigated the radio-opacity of commercially available glass ionomer cements (GICs), flowable resin composites (FRCs) and calcium hydroxide cements (CHCs) and compared this with the radio-opacity of enamel, dentine and aluminium stepwedge. 16 GICs, 8 FRCs and 4 CHCs were analysed.Methods:Three sets of three samples were prepared: 1 mm, 2 mm and 3 mm thickness for GIC and FRC and 1 mm thickness for CHC. Specimens of enamel and dentine with the same thicknesses were obtained. As a control, an aluminium stepwedge was used. Radiographs were taken with a digital Kodak RVG 5000 (0.32 s, 30 cm). The images were analysed using the Image Tool® program (v. 2.00; The University of Texas Health Science Center, San Antonio, TV) to obtain the mean grey values.Results:Analysis of variance was used to investigate the significance of differences among the groups. For pairwise comparisons, the Tukey test was applied (p < 0.05). The GICs Ionomaster (Wilcos, Petrópolis, Brazil), Maxxion (FGM, Joinvill...

Composite resins might be susceptible to degradation and staining when in contact with some foods and drinks. This study evaluated color alteration and changes in microhardness of a microhybrid composite after immersion in different colored foods and determined whether there was a correlation between these two variables. Eighty composite disks were randomly divided into 8 experimental groups (n = 10): kept dry; deionized water; orange juice; passion fruit juice; grape juice; ketchup; mustard and soy sauce. The disks were individually immersed in their respective test substance at 37 ºC, for a period of 28 days. Superficial analysis of the disk specimens was performed by taking microhardness measurements (Vickers, 50 g load for 45 seconds) and color alterations were determined with a spectrophotometer (CINTRA 10- using a CIEL*a*b* system, 400-700 nm wavelength, illuminant d65 and standard observer of 2º) at the following times: baseline (before immersion), 1, 7, 14, 21 and 28 days. Results were analyzed by ANOVA and Tukey's test (p < 0.05). Both variables were also submitted to Pearson's correlation test (p < 0.05). The passion fruit group underwent the greatest microhardness change, while the mustard group suffered the greatest color alteration. Significant positive correlation was found between the two variables for the groups deionized water, grape juice, soy sauce and ketchup. Not all color alteration could be associated with surface degradation.

Objective: The aim of the present in vitro study was to evaluate, using two different methodologies, the effectiveness of pulsed Nd:YAG laser irradiation associated with topical acidulated phosphate fluoride (APF) for preventing enamel erosion and structure loss under regimes of erosion and abrasion or erosion only. Background Data: An increased incidence of noncarious lesions (erosion and abrasion) has been observed, consequently new preventative therapies have been proposed. Materials and Methods: Two different methodologies were performed. For the first, 100 bovine crowns were submitted to four different treatments ( n = 25): no treatment (control), 4 min application of APF, Nd:YAG laser irradiation (1 W, 100 mJ, 10 Hz, 141.5 J/cm ² ), and Nd:YAG laser irradiation + 4 min of APF. After the specimens were exposed to citric acid (2% w/v; 30 min), they were submitted to 5000 brushing cycles. Specimen mass was measured before and after the treatments. For the second methodology, 20 human crowns were embedded in acrylic resin and cut surfaces were exposed and polished. The specimens were divided into four groups ( n = 10): no treatment (control), APF for 4 min, Nd:YAG laser irradiation (1 W, 100 mJ, 10 Hz, 125 J/cm ² ), and Nd:YAG laser irradiation + APF. The samples were then immersed in citric acid (2% w/v; 90 min). Vickers hardness was obtained before and after the treatments. Results: The Nd:YAG laser irradiation + APF (bovine and human enamel) was more effective and yielded statistically significant results for surface microhardness and enamel wear. Conclusion: Nd:YAG laser irradiation associated with APF reduced bovine enamel wear and human enamel softening when samples were submitted to a regime of erosion and abrasion or erosion only in vitro .