Biochar produced from low-value forest biomass can provide substantial benefits to ecosystems and mitigate climate change-induced risks such as forest fires. Forest residues from restoration activities and timber harvest and biochar itself are bulky and thus incur high logistic costs, so are considered major bottlenecks for the commercialization of the biochar industry. The objectives of this study were to assess the environmental footprints and techno-economic feasibility of converting forest residues in Pacific Northwest United States into biochar pellets using portable systems followed by delivery of the final product to end-users for land application (dispersion). Two portable systems (Biochar Solutions Incorporated (BSI) and Air Curtain Burner (ACB)) were considered for biochar production. A cradle-to-grave lifecycle assessment (LCA) and a discounted cash flow analysis method were used to quantify the environmental impacts and minimum selling price (MSP) of biochar. The global warming (GW) impact of biochar production through BSI and ACB was estimated to be 306–444, and 750–1016 kgCO₂eq/tonne biochar applied to the field, respectively. The MSP of biochar produced through BSI and ACB was 1674–1909 and 528–1051 USD/tonne biochar applied to the field, respectively. Pelletizing of biochar reduced GW impacts during outbound logistics (~8–20%) but increased emissions during pelletizing (~1–9%). Results show the BSI system was a more viable option in terms of GW impact, whereas the ACB system can produce biochar with lower MSP. The results of the study conclude that the production of biochar pellets through the two portable systems and applied to fields can be both an environmentally beneficial and economically viable option.

We replaced a control peat medium with up to 75% biochar on a volumetric basis in three different forms (powder, BC; pyrolyzed softwood pellets, PP; composite wood-biochar pellets, WP), and under two supplies of nitrogen fertilizer (20 or 80 mg N) subsequently grew seedlings with a comparable morphology to the control. Using gravimetric methods to determine irrigation frequency and exponential fertilization to ensure all treatments received the same amount of N at a given point in the growing cycle, we successfully replaced peat with 25% BC and up to 50% PP. Increasing the proportion of biochar in the media significantly increased pH and bulk density and reduced effective cation exchange capacity and air-filled porosity, although none of these variables was consistent with resultant seedling growth. Adherence to gravimetric values for irrigation at an 80% water mass threshold in the container revealed that the addition of BC and WP, but not PP, required adjustments to the irrigation schedule. For future studies, we encourage researchers to provide more details about bulk density, porosity, and irrigation regime to improve the potential inference provided by this line of biochar and growing media work.

The development of adhesives that have good initial adhesion (tack) that provides improved mat integrity during shape-forming of wood composites has been the subject of recent research. Hybrid adhesives were made based on thermosetting phenol-formaldehyde (PF), to which three tacky adhesives were added: high tack fish glue (FG), dextrin glue (DX) and a commercial acrylic, pressure-sensitive adhesive (PSA). Tacky adhesives were blended with PF at weight levels of 25%, 50% and 75%. The time-dependent tack development of the resulting hybrid adhesives was evaluated by means of a texture analyzer. The bond strength of adhesives was measured after curing by shear block test. PF/DX blends exhibited the highest tack during longer open times, while blends of PF and FG had low tack during shorter times. PF/PSA blends lost their bond strength completely after being heated at the curing temperature of PF. PF/FG blends did not show a significant decrease in bond strength compared to pure PF. The addition of DX had no effect on shear strength at ratios <75%.

The interfacial shear strength (τ _i) between magnesium phosphate ceramics (MPC) and sugar maple (Acer saccharum) has been evaluated by means of a pullout test method. The binder system monopotassium phosphate (MKP) and magnesium oxide (MgO) resulted in the highest τ _i at a MKP/MgO ratio of 3:1. The influence of the levels of MPC binder and aggregates on the interfacial properties has been observed based on a mixture design model. The aggregates were Portland cement (PC), wollastonite (WO), and vitrified calcium aluminosilicates (VCAS). The MPC binder level was the primary factor influencing τ _i, while WO and VCAS can mutually promote τ _i. However, τ _i is decreased when PC is mixed with the two other aggregates. The environmental durability of VCAS-based MPC (V-MPC), PC-based MPC (C-MPC), and WO-based MPC (W-MPC) was assessed by treatments at conditioning (90% relative humidity) and water immersion. The V-MPC/maple has very poor moisture performance, while the C-MPC/maple and W-MPC/maple had reduced interfacial shear stresses but still maintained bond integrity unlike the V-MPC.