The increase in bacterial resistance to one or several antibiotics has become a global health problem. Recently, nanomaterials have become a tool against multidrug-resistant bacteria. The metal and metal oxide nanoparticles are one of the most studied nanomaterials against multidrug-resistant bacteria. Several in vitro studies report that metal nanoparticles have antimicrobial properties against a broad spectrum of bacterial species. However, until recently, the bacterial resistance mechanisms to the bactericidal action of the nanoparticles had not been investigated. Some of the recently reported resistance mechanisms include electrostatic repulsion, ion efflux pumps, expression of extracellular matrices, and the adaptation of biofilms and mutations. The objective of this review is to summarize the recent findings regarding the mechanisms used by bacteria to counteract the antimicrobial effects of nanoparticles.

The main microorganism associated with the failure of endodontic treatments is Enterococcus faecalis. Although several endodontic therapeutics have demonstrated antimicrobial activity against E. faecalis, the antimicrobial effectiveness of chitosan (CsNPs) and silver nanoparticles (AgNPs) included into conventional endodontic sealers for endodontic therapies is still unclear. The objective of this study was to evaluate the antibacterial activity increment (AAI) of endodontic sealers containing CsNPs and AgNPs as well as some chemical components against E. faecalis by direct contact assays. CsNPs and AgNPs were synthesized by reduction and ionic gelation methods, respectively. Nanoparticles were characterized by dynamic light scattering and energy dispersive X-ray analysis. The bactericidal activity was tested on monolayers on agar plates and collagen membrane surface assays against E. faecalis. The size of CsNPs was 70.6±14.8 nm and zeta potential was 52.0±5.4 mV; the size of AgNPs was 54.2±8.5 nm, and zeta potential was –48.4±6.9 mV. All materials, single or combined, showed an AAI, especially when CsNPs, chlorhexidine (Chx), and the combination of CsNPs-Chx were added. However, the combination of CsNPs-Chx showed the highest (55%) AAI, followed by Chx (35.5%) and CsNPs (11.1%), respectively. There was a significant statistical difference in all comparisons (p < 0.05). Tubliseal (40%) and AH Plus (32%) sealants showed a higher AAI on E. faecalis in the monolayer test and collagen membrane assay analyzed by scanning electron microscopy. Tubliseal and AH plus sealers combined with nanoparticles, especially CsNPs-Chx, could be used for conventional endodontic treatments in the control of E. faecalis bacteria.

Endodontic persistent infections are often mediated by bacterial biofilms. This mode of bacterial growth is characterized by the presence of a matrix mainly composed of extracellular polymeric substances (EPSs) that protect the encased microorganisms. To establish better control and disinfection protocols, elucidation of the main components of biofilm matrices present in endodontic infections is required. The aim of the present study was to characterize the principal components ofE. faecalis,A. naeslundii, and dual-species biofilm matrices by means of Raman spectroscopy and confocal scanning laser microscopy (CSLM) techniques. The total biomass of biofilms was quantified via crystal violet assays, and the monospecies biofilms showed higher biomass than the dual-species biofilms. Raman spectroscopy and confocal laser scanning microscopy were used to identify the biochemical composition and structure of the biofilm matrices. Spectra originating from the biofilms of two endodontic pathogens show the presence of carbohydrates, proteins, fatty acids, and nucleic acids in all samples; however, variation in the levels of expression of these biomolecules allows spectroscopic differentiation of the biofilms using principal component analysis. This study is the first attempt to identify the composition of monospecies and dual-species biofilms of endodontic origin. Our data provides an important approach to the understanding of molecular dynamics of endodontic infections.

The objective was to evaluate the effect of adding silver nanoparticles into three commercial adhesive systems (Excite™, Adper Prompt L-Pop™ and AdheSE™). Nanoparticles were prepared by a chemical method then mixed with the commercial adhesive systems. This was later applied to the fluorotic enamel, and then micro-tensile bond strength, contact angle measurements and scanning electron microscopy observations were conducted. The commercial adhesive systems achieved the lowest micro-tensile bond strength (Excite™: 11.0±2.1, Adper Prompt L-Pop™: 14.0±5.4 and AdheSE™: 16.0±3.0 MPa) with the highest adhesive failure mode related with the highest contact angle (46.0±0.6º, 30.0±0.5º and 28.0±0.4º respectively). The bond strength achieved in all the experimental adhesive systems (19.0±5.4, 20.0±4.0 and 19.0±3.5 MPa respectively) was statistically higher (p<0.05) than the control and showed the highest cohesive failures related to the lowest contact angle. Adding silver nanoparticles in order to decrease the contact angle improve the adhesive system wetting and its bond strength.