In this work, a multi-functional nanoparticle (TiO₂-KH570-DOPO) has been successfully synthesized through the attachment of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO)-methacryloxy propyl trimethoxyl silane on the surface of titanium dioxide (TiO₂). Supercritical carbon dioxide was used as the solvent in order to increase the grafting level. The chemical structure of TiO₂-KH570-DOPO was fully characterized using Fourier transform infrared spectra, thermogravimetric analysis and transmission electron microscopy. The modified TiO₂ was incorporated into flexible polyurethane foam (FPUF). The fire performance of FPUF blends was evaluated using microscale combustion calorimetry. Peak heat release rate and total heat release values were reduced from 657.0 W/g and 28.9 kJ/g for neat FPUF sample to 519.2 W/g and 26.8 kJ/g of FPUF specimen containing 10 wt % of TiO₂-KH570-DOPO. Analysis of thermal stability and the observation of char formation suggests that TiO₂-KH570-DOPO is active in the condensed phase.

In this work, silica aerogel was modified by 9,10-dihydro-9-oxa-10-phosphaphenanthrene-1-oxide (DOPO). Then DOPO-immobilized silica aerogel nanoparticles were used as a flame retardant to prepare flame-retardant polyurethane foams. Microscale combustion calorimeter and cone calorimeter tests were employed to evaluate the flame retardancy of polyurethane foams. It was found that both the heat release rate and the total heat release of the composites were reduced with the incorporation of DOPO immobilized silica aerogel. It is speculated that the DOPO-immobilized silica aerogel nanoparticles can inhibit the degradation of polyurethane and catalyze the formation of carbonaceous carbon on the surface.