The structural and electronic recovery pathways of a photoexcited ultrathin vanadium dioxide (VO${}_2$) film at nanosecond time scales have been studied using time-resolved x-ray diffraction and transient optical absorption techniques. The recovery pathways from the tetragonal metallic phase to the monoclinic insulating phase are highly dependent on the optical pump fluence. At pump fluences higher than the saturation fluence of 14.7 mJ/cm${}^2$, we observed a transient structural state with lattice parameter larger than that of the tetragonal phase, which is decoupled from the metal-to-insulator phase transition. Subsequently, the photoexcited VO${}_2$ film recovered to the ground state at characteristic times dependent upon the pump fluence as a result of heat transport from the film to the substrate. We present a procedure to measure the time-resolved film temperature by correlating photoexcited and temperature-dependent x-ray diffraction measurements. A thermal transport model that incorporates changes of the thermal parameters across the phase transition reproduces the observed recovery dynamics. The optical excitation and fast recovery of ultrathin VO${}_2$ films provides a practical method to reversibly switch between the monoclinic insulating and tetragonal metallic state at nanosecond time scales.

Cellulose nanofibrils (CNFs) are high aspect ratio, natural nanomaterials with high mechanical strength-to-weight ratio and promising reinforcing dopants in polymer nanocomposites. In this study, we used CNFs and oxidized CNFs (TOCNFs), prepared by a 2,2,6,6-tetramethylpiperidine-1-oxyl radical (TEMPO)-mediated oxidation process, as reinforcing agents in poly(vinylidene fluoride) (PVDF). Using high-shear mixing and doctor blade casting, we prepared free-standing composite films loaded with up to 5 wt % cellulose nanofibrils. For our processing conditions, all CNF/PVDF and TOCNF/PVDF films remain in the same crystalline phase as neat PVDF. In the as-prepared composites, the addition of CNFs on average increases crystallinity, whereas TOCNFs reduces it. Further, addition of CNFs and TOCNFs influences properties such as surface wettability, as well as thermal and mechanical behaviors of the composites. When compared to neat PVDF, the thermal stability of the composites is reduced. With regards to bulk mechanical properties, addition of CNFs or TOCNFs, generally reduces the tensile properties of the composites. However, a small increase (~18%) in the tensile modulus was observed for the 1 wt % TOCNF/PVDF composite. Surface mechanical properties, obtained from nanoindentation, show that the composites have enhanced performance. For the 5 wt % CNF/PVDF composite, the reduced modulus and hardness increased by ~52% and ~22%, whereas for the 3 wt % TOCNF/PVDF sample, the increase was ~23% and ~25% respectively.