Surface x-ray diffraction has been employed to elucidate the surface structure of the $(011)-(2\times 1)$ termination of rutile ${\mathrm{TiO}}_2$. The data are inconsistent with previously proposed structures. Instead, an entirely unanticipated geometry emerges from the structure determination, which is terminated by zigzag rows of twofold coordinated oxygen atoms asymmetrically bonded to fivefold titanium atoms. The energetic stability of this structure is demonstrated by ab initio total energy calculations.

Metal-halide perovskites show remarkably clean semiconductor behaviour, as evidenced by their excellent solar cell performance, in spite of the presence of many structural and chemical defects. Here, we show how this clean semiconductor performance sets in during the earliest phase of conversion from the metal salts and organic-based precursors and solvent, using simultaneous in situ synchrotron X-ray and in operando current–voltage measurements on films prepared on interdigitated back-contact substrates. These structures function as working solar cells as soon as sufficient semiconductor material is present across the electrodes. We find that at the first stages of conversion from the precursor phase, at the percolation threshold for bulk conductance, high photovoltages are observed, even though the bulk of the material is still present as precursors. This indicates that at the earliest stages of perovskite structure formation, the semiconductor gap is already well-defined and free of sub-gap trap states. The short circuit current, in contrast, continues to grow until the perovskite phase is fully formed, when there are bulk pathways for charge diffusion and collection. This work reveals important relationships between the precursors conversion and device performance and highlights the remarkable defect tolerance of perovskite materials.