The design of drilling fluids is very important for the drilling operation success. The rheological properties play a key role in the performance of the drilling fluid. Therefore, studying the mud rheological properties of the water-based drilling fluid based on bentonite is essential. The main objectives of this study are to address the effect of pH changes on the rheological and filtration properties of the water-based drilling fluid based on bentonite and to provide a recommended pH range for this drilling fluid for a safe and high-performance drilling operation. Different samples of the water-based drilling fluid based on bentonite with different pH values were prepared, and the rheological properties such as plastic viscosity, yield point, and gel strength were measured. After that, the filtration test was performed under 300 psi differential pressure and 200 °F. The pH for the water-based drilling fluid based on bentonite significantly affects the mud rheology. The shear stress and shear rate relation were varying with the change in the pH. Increasing the pH from 8 to 12 resulted in decreasing the plastic viscosity by 53% and the yield point by 82%, respectively. The ratio of yield point / plastic viscosity was 1.4 for pH of 8 while it decreased to 0.5 for a pH of 11 and 12. There was a significant decrease in the gel strength readings by increasing the pH. The filtrate volume and filter cake thickness increased by increasing pH. The filtration volume increased from 9.5 cm³ to 12.6 cm³ by increasing the pH from 9 to 12. The filter cake thickness was 2 mm at 9 pH, while it was increased to 3.6 mm for 12 pH. It is recommended from the results to keep the pH of water-based drilling fluid based on bentonite in the range of 9 to 10 as it provides the optimum mud rheological and filtration properties. The findings of this study illustrated that keeping the pH in the range of 9 to 10 will reduce the plastic viscosity that will help in increasing the rate of penetration and reducing the required pump pressure to circulate the mud to the surface which will help to sustain the drilling operation. In addition, reducing the filtrate volume will produce a thin filter cake which will help in avoiding the pipe sticking and protect the environment. In general, optimizing the pH of the water-based drilling fluid based on bentonite in the range of 9 to 10 will improve the drilling operation and minimize the total cost.

Drilling high-pressure high-temperature (HPHT) wells requires a special fluid formulation that is capable of controlling the high pressure and is stable under the high downhole temperature. Barite-weighted fluids are common for such purpose because of the good properties of barite, its low cost, and its availability. However, solids settlement is a major problem encountered with this type of fluids, especially at elevated downhole temperatures. This phenomenon is known as barite sag, and it is encountered in vertical and directional wells under static or dynamic conditions leading to serious well control issues. This study aims to evaluate the use of barite-ilmenite mixture as a weighting agent to prevent solids sag in oil-based muds at elevated temperatures. Sag test was conducted under static conditions (vertical and inclined) at 350 °F and under dynamic conditions at 120 °F to determine the optimum ilmenite concentration. Afterward, a complete evaluation of the drilling fluid was performed by monitoring density, electrical stability, rheological and viscoelastic properties, and filtration performance to study the impact of adding ilmenite on drilling fluid performance. The results of this study showed that adding ilmenite reduces sag tendency, and only 40 wt.% ilmenite (from the total weighting material) was adequate to eliminate barite sag under both static and dynamic conditions with a sag factor of around 0.51. Adding ilmenite enhanced the rheological and viscoelastic properties and the suspension of solid particles in the drilling fluid, which confirmed sag test results. Adding ilmenite slightly increased the density of the drilling fluid, with a slight decrease in the electrical stability within the acceptable range of field applications. Moreover, a minor improvement in the filtration performance of the drilling fluid and filter cake sealing properties was observed with the combined weighting agent. The findings of this study provide a practical solution to the barite sag issue in oil-based fluids using a combination of barite and ilmenite powder as a weighting agent to drill HPHT oil and gas wells safely and efficiently with such type of fluids.

Barite sag is a serious problem encountered while drilling high-pressure/high-temperature (HPHT) wells. It occurs when barite particles separate from the base fluid leading to variations in drilling fluid density that may cause a serious well control issue. However, it occurs in vertical and inclined wells under both static and dynamic conditions. This study introduces a combined barite–ilmenite weighting material to prevent the barite sag problem in water-based drilling fluid. Different drilling fluid samples were prepared by adding different percentages of ilmenite (25, 50, and 75 wt.% from the total weight of the weighting agent) to the base drilling fluid (barite-weighted). Sag tendency of the drilling fluid samples was evaluated under static and dynamic conditions to determine the optimum concentration of ilmenite which was required to prevent the sag issue. A static sag test was conducted under both vertical and inclined conditions. The effect of adding ilmenite to the drilling fluid was evaluated by measuring fluid density and pH at room temperature, and rheological properties at 120 °F and 250 °F. Moreover, a filtration test was performed at 250 °F to study the impact of adding ilmenite on the drilling fluid filtration performance and sealing properties of the formed filter cake. The results of this study showed that adding ilmenite to barite-weighted drilling fluid increased fluid density and slightly reduced the pH within the acceptable pH range (9–11). Ilmenite maintained the rheology of the drilling fluid with a minimal drop in rheological properties due to the HPHT conditions, while a significant drop was observed for the base fluid (without ilmenite). Adding ilmenite to the base drilling fluid significantly reduced sag factor and 50 wt.% ilmenite was adequate to prevent solids sag in both dynamic and static conditions with sag factors of 0.33 and 0.51, respectively. Moreover, HPHT filtration results showed that adding ilmenite had no impact on filtration performance of the drilling fluid. The findings of this study show that the combined barite–ilmenite weighting material can be a good solution to prevent solids sag issues in water-based fluids; thus, drilling HPHT wells with such fluids would be safe and effective.

Drilling multilateral and horizontal wells through tight gas reservoirs is a very difficult task. The drilling fluid should be designed to reduce both fluid and solid invasion into the tight formation to avoid formation damage by aqueous phase trapping. The objective of this paper is to assess the effect of sodium silicate on the drilling fluid properties such as rheological and filtration properties. Rheological properties (RPs) were measured at different temperatures while the filtration test was performed at 300 °F and 300 psi differential pressure. A retained permeability calculation was determined to confirm the prevention of solid invasion. The rheological properties results confirmed that the optimal concentration of sodium silicate (SS) was 0.075 wt.% and at the same time, the temperature has no effect on the SS optimum concentration. Using 0.075 wt.% of SS reduced the filtrate volume by 53% and decreased the filter cake thickness by 65%. After mechanical removal of the filter cake, the return permeability of the tight sandstone core was 100% confirming the prevention of solid invasion. The computer tomography (CT) scanner showed that the CT number before and after the filtration test was very close (almost the same) indicating zero solid invasion and prevention of the formation damage.