In the present work, PbO-x wt% Al₂O₃ nanocomposites (where x = 0, 10, 20, 30, 40, 50, 60, 70, and 100 wt%) were prepared by a microwave irradiation method. Their structural parameters, morphology, and chemical bonds, were investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), and Fourier-transform infrared spectroscopy (FTIR). It was noticed that the produced phases have an orthorhombic crystal structure and the smaller average crystallite sizes were formed when the ratio of Al₂O₃ is 40 wt%. The FTIR analysis reveals the formation of various bonds between Al or Pb and O. The TEM analysis reveals that the PbO-x%Al₂O₃ composites (x = 20, 40, and 60), composed of dense particles, and their size are smaller compared to the pure Al₂O₃ sample. The optical bandgap obeys the direct allowed transition and decreases from 4.83 eV to 4.35 eV as the PbO ratio in the composites increases from 0 to 100%. The intensity of the photoluminescence emission, at the same wavelength, increases as the PbO ratio increases from 0% to 60% implying that increasing the PbO content increases the capacity of free carriers within the trap centers. The prepared composites are used as a catalyst to remove the methylene blue (MB) from the wasted water under UV-visible or visible light irradiations. The photocatalytic degradation of MB was investigated by applying various kinetic models. It was found that the PbO-30% Al₂O₃, and PbO-40% Al₂O₃ composites are the best ones amongst other compositions. Furthermore, the pseudo-second-order model is the best model for describing the deterioration mechanism among the models studied. The formed composites could be suitable for the degradation of organic dyes for water purification as well as applications that required a higher optical bandgap.

Acrylic polymer/cement nanocomposites in dark and light colors have been developed for coating floors and swimming pools. This work aims to emphasize the effect of cement filling on the mechanical parameters, thermal stability, and wettability of acrylic polymer. The preparation was carried out using the casting method from acrylic polymer coating solution, which was added to cement nanoparticles (65 nm) with weight concentrations of (0, 1, 2, 4, and 8 wt%) to achieve high-quality specifications and good adhesion. Maximum impact strength and Hardness shore A were observed at cement ratios of 2 wt% and 4 wt%, respectively. Changing the filling ratio has a significant effect on the strain of the nanocomposites. The contact angle was increased as the concentration of additives and cement increased, indicating that the synthesized coating is not hydrophilic and does not allow water permeability through it. The results show that the acrylic polymer/cement with a cement ratio of 8 wt% is the best nanocomposite for high-efficiency waterproofing.

The differential thermal analysis (DTA) is utilized to determine the phase boundary and phase equilibria of Co–Cu alloy having a miscibility gap. Regions for various phase i.e., spinodal and coherent binodal, peritectic, magnetic and the transformation from the two phases to α phase transformations are distinctly determined for the Co–13 at%Cu alloy. The obtained results might indicate the continuity of the decomposition kinetics at the boundary between instable and the metastable regions but an activation barrier is needed. The activation energy for the magnetic transformation is determined to be 182.2 ± 2.1 kJ mol⁻¹.

Silver/polyvinyl alcohol (Ag/PVA) nanocomposite films were synthesized via solution casting with varying concentrations of Ag nanoparticles (1–5 wt%). A comprehensive investigation was conducted to understand the influence of Ag content on the structural, optical, mechanical, thermal, electrical, and antibacterial properties of the composites. UV-Vis spectroscopy revealed a red shift in absorption peaks and a reduction in the optical band gap, which decreased from 3.78 eV for pure PVA to 3.37 eV for the 5 wt% Ag composite. FTIR and SEM analyses confirmed successful nanoparticle incorporation and morphological changes. The nanocomposites exhibited enhanced tensile strength, elongation at break, Young’s modulus, and hardness due to strong interfacial interactions. The addition of Ag also increased hydrophobicity and imparted effective antibacterial activity. The electrical and thermal properties showed significant improvement: AC conductivity increased from 5.8 × 10⁻⁹ to 1.01 × 10⁻⁴ S/cm with Ag content, while the dielectric constant decreased. A high DC conductivity of 1.5 × 10⁵ S/cm was achieved with only 3 wt% Ag. Thermal conductivity also rose from 0.27 W/m·K for pure PVA to 0.92 W/m·K for the 5 wt% composite. These results demonstrate that Ag/PVA nanocomposites are promising multifunctional materials for flexible electronics, combining tunable optoelectronic properties with enhanced mechanical, thermal, and antibacterial performance.