Polystyrene (PS) dissolved in a mixture of N, N-dimethylformamide (DMF) and/or tetrahydrofuran (THF) was electrospun to prepare fibers with sub-micron diameters. The effects of electrospinning parameters, including solvent combinations, polymer concentrations, applied voltage on fiber morphology, as well as tensile and hydrophobic properties of the fiber mats were investigated. Scanning electron microscope (SEM) images of electrospun fibers (23% w/v PS solution with applied voltage of 15 kV) showed that a new type of fiber with double-strand morphology was formed when the mass ratio of DMF and THF was 50/50 and 25/75. The tensile strength of the PS fiber film was 1.5 MPa, indicating strong reinforcement from double-strand fibers. Bead-free fibers were obtained by electrospinning 40% (w/v) PS/DMF solution at an applied voltage of 15 kV. Notably, when the ratio of DMF and THF was 100/0, the maximum contact angle (CA) value of the electrospun PS films produced at 15 kV was 148°.

Radiative cooling fabric creates a thermally comfortable environment without energy input, providing a sustainable approach to personal thermal management. However, most currently reported fabrics mainly focus on outdoor cooling, ignoring to achieve simultaneous cooling both indoors and outdoors, thereby weakening the overall cooling performance. Herein, a full-scale structure fabric with selective emission properties is constructed for simultaneous indoor and outdoor cooling. The fabric achieves 94% reflectance performance in the sunlight band (0.3–2.5 µm) and 6% in the mid-infrared band (2.5–25 µm), effectively minimizing heat absorption and radiation release obstruction. It also demonstrates 81% radiative emission performance in the atmospheric window band (8–13 µm) and 25% radiative transmission performance in the mid-infrared band (2.5–25 μm), providing 60 and 26 W m⁻² net cooling power outdoors and indoors. In practical applications, the fabric achieves excellent indoor and outdoor human cooling, with temperatures 1.4–5.5 °C lower than typical polydimethylsiloxane film. This work proposes a novel design for the advanced radiative cooling fabric, offering significant potential to realize sustainable personal thermal management.

Transitional Properties of Cotton Fibers from Cellulose I to Cellulose II Structure