Optical properties of ZnO nanoparticles capped with polymers were investigated. Polyethylene glycol (PEG) and polyvinyl pyrrolidone (PVP) were used as capping reagents. ZnO nanoparticles were synthesized by the sol-gel method. Fluorescence and absorption spectra were measured. When we varied the timing of the addition of the polymer to the ZnO nanoparticle solution, the optical properties were drastically changed. When PEG was added to the solution before the synthesis of ZnO nanoparticles, the fluorescence intensity increased. At the same time, the total particle size increased, which indicated that PEG molecules had capped the ZnO nanoparticles. The capping led to surface passivation, which increased fluorescence intensity. However, when PEG was added to the solution after the synthesis of ZnO nanoparticles, the fluorescence and particle size did not change. When PVP was added to the solution before the synthesis of ZnO nanoparticles, aggregation of nanoparticles occurred. When PVP was added to the solution after the synthesis of ZnO nanoparticles, fluorescence and particle size increased. This improvement of optical properties is advantageous to the practical usage of ZnO nanoparticles, such as bioimaging

A YVO₄:Eu³⁺ colloid with an interesting nanostructure was formed by pulsed laser ablation in deionized water without any additives or surfactants. Analyses of particle morphology, composition and optical properties were accomplished by SEM, TEM, EDS PL and UV-vis. Ovoid-like particles formed by the agglomeration of numerous nanocrystals were observed by SEM and TEM, while EDS with area-mode analysis revealed that the content of dopant ion was well retained within the nanoparticles. In addition, the formation mechanism is deduced and discussed for the first time in this research. The findings of this study could provide new insights into the understanding of laser-induced oxide materials and offer an opportunity for other research groups to pursue red emitting nanophosphors with outstandingly purity.

The effect of laser wavelength on size and morphology of silicon nanoparticles are studied. To prepare nanoparticles, laser ablation in liquid technique is employed. Absorption spectra demonstrate that with laser wavelength of 532 nm, solution with higher concentration can be prepared in comparison with one obtained from laser wavelength of 1064 nm. Transmission electron microscope (TEM) images reveal nanoparticles with spherical shape from samples produced by both laser wavelengths. However, smaller particles size are obtained from sample prepared by laser wavelength of 532 nm. Raman spectra and photoluminescence (PL) spectra further support the existence of smaller crystal size in this sample.

Optics InfoBase is the Optical Society's online library for flagship journals, partnered and copublished journals, and recent proceedings from OSA conferences.