Standard experimental research works are aimed at optimization of Selective Laser Melting (SLM) parameters in order to produce material with relative density over 99% and possibly the highest scanning speed. Typically, cuboidal specimens with arbitrarily selected dimensions are built. An optimum set of parameters, determined on such specimens, is used for building parts with variable cross-section areas. However, it gives no guarantee that the density of variable-section parts produced with so selected parameters will be as high as that of the specimens measured during the parameters optimization process. The goal of this work was to improve the process of SLM parameter selection according to the criterion of maximum relative density, based on the example of AISI H13 tool steel (1.2344). A selection method of scanning strategy ensuring relative density of parts over 99%, irrespective of their dimensions, was determined. The specimens were produced using several variants of support structures. It was found that proper selection of the support strategy prevents development of columnar pores.

Inconel 718 (In718) is the most widely used nickel-based alloy in additive manufacturing due to its favorable processability. However, In718’s high-temperature performance is not suited for the most demanding applications in the aerospace industry. Therefore, in this study, Inconel 718 powder was coated with 3% wt. rhenium (In718-Re) using AM’s in situ alloying capabilities to improve high-temperature properties. The proposed alloy’s mechanical performance was evaluated, focusing on the effects of post-process heat treatment and hot isostatic pressing following the laser-based powder bed fusion of metals (PBF-LB/M) processing. Static tensile tests conducted at room temperature and elevated temperatures (650 °C and 760 °C) demonstrated that the alloy has comparable strength to pure In718 according to ASTM F3055-14a—an ultimate tensile strength of 1247 MPa, yield strength of 909 MPa, and almost 2× higher elongation of 23.8%. Fatigue tests at room temperature indicated a fatigue limit below 400 MPa for 10⁷ cycles. Fractographic analysis revealed that fatigue performance was primarily impacted by a lack of fusion defects inherent to the PBF-LB/M process, highlighting the need for optimized powder preparation and processing parameters to minimize defect formation. While rhenium addition shows limited benefits in Inconel 718, this study underscores the potential of in situ alloying through powder surface modification as a flexible method for incorporating high-melting-point elements into nickel-based alloys for tailored alloy design in additive manufacturing.