The effect of target phosphorus (P) content on the precipitates, microstructure, texture, magnetic properties, and mechanical properties of low-carbon (C) and low-silicon (Si) non-oriented electrical steel (NOES) was investigated and the influence mechanism was clarified. The results indicate that the precipitates in the steels are mainly aluminum (Al)-manganese (Mn)-Si-bearing complex nitrides ((Al,Si,Mn)_xN_y) and P-bearing complex nitrides ((Al,Si,Mn)_xN_y-P). Increasing target phosphorus content in the steels decreases (Al,Si,Mn)_xN_y, and increases (Al,Si,Mn)_xN_y-P. The number density of the precipitates is the lowest, and the average size of the precipitates and grain size of the finished steel is the largest in the samples with target P content at the 0.14% level (0.14%P-targeted). The average grain size and microstructure homogeneity of the steels are influenced by the addition of phosphorus. The content of the {111} component decreases, and the favorable texture increases after phosphorus is added to the steel. The magnetic induction of the steel is improved. Grain refinement and microstructure inhomogeneity lead to an iron loss increase after target phosphorus content increases in the steel. The best magnetic induction B₅₀ is 1.765 T in the 0.14%P-targeted samples. The tensile strength and yield strength are improved owing to solid solution strengthening and the grain refinement effect of phosphorus added to the steels.

Argon stirring is one of the most widely used metallurgical methods in the secondary refining process as it is economical and easy, and also an important refining method in clean steel production. Aiming at the issue of poor homogeneity of composition and temperature of a bottom argon blowing ladle molten steel in a Chinese steel mill, a 1:5 water model for 110 t ladle was established, and the mixing time and interface slag entrainment under the different conditions of injection modes, flow rates and top slag thicknesses were investigated. The flow dynamics of argon plume in steel ladle was also discussed. The results show that, as the bottom blowing argon flow rate increases, the mixing time of ladle decreases; the depth of slag entrapment increases with the argon flow rate and slag thickness; the area of slag eyes decreases with the decrease of the argon flow rate and increase of slag thickness. The optimum argon flow rate is between 36–42 m³/h, and the double porous plugs injection mode should be adopted at this time.