The use of fast-growing plantation eucalypt (i.e., pulpwood eucalypt) in the construction of high-value structural products has received special attention from the timber industry in Australia and worldwide. There is still, however, a significant lack of knowledge regarding the physical and mechanical properties of the lumber from such plantation resources as they are mainly being managed to produce woodchips. In this study, the physical and mechanical properties of lumber from a 16-year-old pulpwood Eucalyptus nitens H.Deane & Maiden resource from the northeast of Tasmania, Australia was evaluated. The tests were conducted on 318 small wood samples obtained from different logs harvested from the study site. The tested mechanical properties included bending modulus of elasticity (10,377.7 MPa) and modulus of rupture (53 MPa), shear strength parallel (5.5 MPa) and perpendicular to the grain (8.5 MPa), compressive strength parallel (42.8 MPa) and perpendicular to the grain (4.1 MPa), tensile strength perpendicular to the grain (3.4 MPa), impact bending (23.6 J/cm²), cleavage (1.6 kN) and Janka hardness (23.2 MPa). Simple linear regression models were developed using density and moisture content to predict the mechanical properties. The variations in the moisture content after conventional kiln drying within randomly selected samples in each test treatment were not high enough to significantly influence the mechanical properties. A relatively high variation in the density values was observed that showed significant correlations with the changes in the mechanical properties. The presence of knots increased the shear strength both parallel and perpendicular to the grain and significantly decreased the tensile strength of the lumber. The results of this study created a profile of material properties for the pulpwood E. nitens lumber that can be used for numerical modelling of any potential structural product from such a plantation resource.

Salvaged timber elements often have length limitations, and therefore, their reuse in structural products normally would require additional processing and end-to-end joining. This increases the costs of reusing such materials, which makes them even less attractive to the timber sector. In the presented research, a new approach is proposed for reusing short, salvaged timber elements combined with new (full-scale) timber boards to fabricate dowel-laminated timber (DLT) panels without significant processing or end-to-end joining or gluing. In this approach, salvaged timber elements are pressed in the system in such a way that they can contribute to the bending performance of the DLT panels by resisting compression stress. In order to evaluate the effectiveness, several small-scale and large-scale DLT panels were fabricated. Salvaged plywood tenons were used as connectors. The bending stiffness of the small-scale DLT panels and the first eigenfrequency, damping ratio, bending properties, and failure modes of the large-scale DLT panels were evaluated. The results exhibited that by using the proposed approach, the short, salvaged timber elements can contribute substantially to the bending stiffness of the DLT panels without requiring end-to-end joining or gluing. On average, about a 40% increase in the bending stiffness could be achieved by pressing in the salvaged timber elements, which results in relatively similar stiffness properties compared to conventional DLT panels. One further characteristic is that the failure of the panels, and therefore the panel’s strength, is mainly governed by the quality of the full-scale timber boards instead of the salvaged ones. This can be beneficial for practical use as the qualitative assessment of the strength properties of salvaged timber becomes less critical.

What to Do with Structurally Low-Grade Wood from Australia’s Plantation Eucalyptus; Building Application?