The data for the physicochemical properties viscosity, density, and surface tension obtained by different experimental techniques have been analyzed for liquid Al–Zn, Ag–Sn, Bi–Sn, Cu–Sn, and Sn–Zn eutectic alloys. All experimental data sets have been categorized and described by the year of publication, the technique used to obtain the data, the purity of the samples and their compositions, the quoted uncertainty, the number of data in the data set, the form of data, and the temperature range. The proposed standard deviations of liquid eutectic Al–Zn, Ag–Sn, Bi–Sn, Cu–Sn, and Sn–Zn alloys are 0.8%, 0.1%, 0.5%, 0.2%, and 0.1% for the density, 8.7%, 4.1%, 3.6%, 5.1%, and 4.0% for viscosity, and 1.0%, 0.5%, 0.3%, N/A, and 0.4% for surface tension, respectively, at a confidence level of 95%.

Ga–Sn–Zn eutectic alloy is a non-toxic liquid metal alloy which could be used in a multitude of applications, including as a heat transfer agent, in gas sensing, and in medicine. Alloys containing gallium readily oxidise in air, forming a thin oxide layer that influences the properties of liquid metals and which has not been studied. In this study, the oxide layer formed on Ga–Sn–Zn alloy was transferred at room temperature onto three substrates—quartz, glass and silicon. The contact angle between the liquid alloy and different substrates was determined. The obtained thin oxide films were characterised using atomic force microscopy, X-ray photon spectroscopy, and optical and transmission electron microscopy. The contact angle does not influence the deposition of the layers. It was determined that it is possible to obtain nanometric oxide layers of a few micrometres in size. The chemical composition was determined by XPS and EDS independently, and showed that the oxide layer contains about 90 atom % of gallium with some additions of tin and zinc. The oxides obtained from the eutectic Ga–Sn–Zn liquid alloys appear to be nanocrystalline.