Surface wettability plays an important role in determining the function of a wound dressing. Dressings with hydrophobic surfaces are suitable for bacterial adsorption, however, a hydrophilic surface is needed to improve cell attachment for most anchorage-dependent cell types. Furthermore, the hydrophobicity/hydrophilicity of the surface can be used to direct cellular processes such as cell initial attachment, adhesion, and migration during wound healing. Thus, a surface with an ability to switch their surface wettability improves the practicality of the dressing. In this study, we propose a temporary surface wettability tuning for surface patterning utilizing plasma treatment. Polycaprolactone (PCL) and polydimethylsiloxane (PDMS) surfaces were treated with tetrafluoromethane (CF₄), sulphur hexafluoride (SF₆), and oxygen (O₂) plasma, and the effects on the surface wettability, roughness, and chemical composition were investigated. Based on the contact angle measurement, CF₄ plasma altered surface wettability of PCL and PDMS films to hydrophobic and hydrophilic, respectively. After CF₄ treatment, better attachment of primary mouse embryonic fibroblast cell (3T3) was observed on the treated PDMS surface. Embedding PCL into PDMS generated a hydrophobic-hydrophilic pattern mixture surface, which offers great potential in the tissue engineering field such as cell patterning and guidance.

A thermally activated shape memory polymer based on the mixture of polycaprolactone (PCL) and polydimethylsiloxane (PDMS) was fabricated into the nanofibre mesh using the electrospinning process. The added percentages of the PDMS segment in the PCL-based polymer influenced the mechanical properties. Polycaprolactone serves as a switching segment to adjust the melting temperature of the shape memory electro-spun PCL–PDMS scaffolds to our body temperature at around 37 °C. Three electro-spun PCL–PDMS copolymer nanofibre samples, including PCL₆–PDMS₄, PCL₇–PDMS₃ and PCL₈–PDMS₂, were characterised to study the thermal and mechanical properties along with the shape memory responses. The results from the experiment showed that the PCL switching segment ratio determines the crystallinity of the copolymer nanofibres, where a higher PCL ratio results in a higher degree of crystallinity. In contrast, the results showed that the mechanical properties of the copolymer samples decreased with the PCL composition ratio. After five thermomechanical cycles, the fabricated copolymer nanofibres exhibited excellent shape memory properties with 98% shape fixity and above 100% recovery ratio. Moreover, biological experiments were applied to evaluate the biocompatibility of the fabricated PCL–PDMS nanofibre mesh. Owing to the thermally activated shape memory performance, the electro-spun PCL–PDMS fibrous mesh has a high potential for biomedical applications such as medical shrinkable tubing and wire.

Hydrogel dressings should be adhesive and elastic, while providing excellent functional and aesthetic features. Owing to weak intermolecular forces, various measures are undertaken to improve the hydrogel mechanical properties. Thermo-responsive poly(2-(2-methoxyethoxy)ethyl methacrylate) (poly(MEO₂MA)) hydrogel fabricated with different amounts of di(ethylene glycol) dimethacrylate (DEGDMA) cross-linker was characterised using texture profile analysis. More cross-linking sites incorporated within the hydrogel limit the swelling ability where 1.0 and 10 mol-% of DEGDMA swell by 8.03 and 1.92 times, at 5°C. Hydrogel textural and tensile property correlated with the cross-linker amount. Meanwhile, network structure disentanglement within swollen hydrogel reduced the force required for deformation. Thus, the swelling behaviour, textural and tensile properties were investigated to discern the possible biomedical applications suitable for this hydrogel.