In this paper, class-C fly ash (FA) and ground granulated blast-furnace slag (GGBS)-based geopolymer activated in NaOH and NaOH + Na₂SiO₃ was studied regarding setting time, compressive strength, porosity, microstructure, and formation of crystalline phases. When comparing the effects of alkali type on the FA and GGBS geopolymer composites, results revealed that NaOH has a lesser effect in developing strength and denser microstructure than does NaOH + Na₂SiO_3, since the addition of Na₂SiO₃ provides the silica source to develop more compact structure. Incorporation of Na₂SiO₃ reduced the crystallinity and the paste was more amorphous compared to NaOH activated pastes. The class-C FA and GGBS blends resulted in prolonged setting time, reduced strength, and loose matrix with the increase in fly ash content. The un-reactivity of calcium in blends was observed with increasing fly ash content, leading to strength loss. It is evident from XRD patterns that calcium in fly ash did not contribute in forming C-S-H bond, but formation of crystalline calcite was observed. Furthermore, XRD analyses revealed that the reduction in fly ash leads to the reduction in crystallinity, and SEM micrographs showed the unreactive fly ash particles, which hinder the formation of a denser matrix.

This study focused on the quick initial setting time and the expansion strain that occurs during the early aging of α-calcium sulfate hemihydrate (αHH) and examined the setting, compressive strength, and shrinkage strain of αHH-replaced cement mortar. The results show that the initial setting time significantly decreased with an increase in the αHH replacement ratio. Drastic occurrence of ettringite was observed early in the aging of cement mortar when αHH was substituted into the cement; however, the ettringite was not converted to monosulfate with increasing age and thus was not favorable for the development of the compressive strength. When αHH was substituted into cement, using Portland blast-furnace slag cement (PSC) was more advantageous than using ordinary Portland cement (OPC) for the development of the compressive strength. Meanwhile, the expansion of early age αHH can decrease the shrinkage strain of cement mortar. The generation of ettringite is more effective when αHH is substituted into PSC than into OPC and is thus more effective in suppressing the shrinkage strain.

This paper proposes an estimation equation that can be used to predict the progress of deterioration for various building materials, and an attempt is made to summarize and classify the deterioration phenomena of each material used in a building. The estimation equation classifies three types of deterioration patterns, alignment, convergence, and multiplication, according to the difference in the properties of deteriorating parts. <!----> <!----> <!----> <!---->