The thermal dissipation issue of electronics devices becomes increasingly prominent as they evolve to smaller sizes and more complicated structures. Therefore, the development of materials with excellent heat conduction properties and light weight turns out to be an urgent demand to solve the heat transfer problem of electronics devices with high performance. For this purpose, we put forward an innovative strategy that carbonized dehydroascorbic acid (CDA) be applied to graphene layers for the targeted repair of defects among them and bridge connection of the layers to produce graphene heat conduction materials with excellent properties. Firstly, hydrogen bonds formed from dehydroascorbic acid (DHAA, products of the oxidation of vitamin C) and each of ketone, carboxyl, and oxhydryl groups on graphene layers were absorbed at targeted locations where oxidation graphene produces defects, then targeted repair was conducted for those defects to be filled and for the graphene layers of a small size to grow into large sheet materials with improved continuity by CDA generated in thermally pressing reduction reaction at 800 °C. In our investigation, the planar thermal conductivity of rGO/VC membrane reached 1031.9 ± 10.2 Wm−1K−1, while the added mass content of vitamin C (VC) was 15%. Being a reference, the planar thermal conductivity of primitive graphene membrane was only 610.7 ± 11.7 Wm−1K−1.

The high thermal conductivity and stability, outstanding mechanical properties, and low weight make graphene suitable for many applications in the realm of thermal management, especially in high integration systems. Herein, we report a high-performance, low-temperature reduced graphene oxide/magnetic carbon fiber composite film. Magnetic carbon fibers were prepared using a co-precipitation method, and the graphene oxide solution was prepared using an improved Hummers’ method. The magnetic carbon fibers were orientated by magnetite and immersed in the graphene oxide solution during filtration, followed by annealing at 800 °C. The composite film exhibited improved thermal conductivity (over 600 W/m·K) and mechanical properties (tensile strength of 37.1 MPa and bending cycle of up to 8000). The experimental results illustrate that the graphene in the composite membrane provides heat transfer channels to promote in-plane thermal conductivity, while the magnetic carbon fiber acts as a scaffold to reinforce the mechanical properties and improve the quality of the graphene. Due to the synergistic effect of the graphene and magnetic carbon, this composite has wide potential applications in heat dissipation.