Nanoporous anodic aluminum oxide (AAO) films play an important role in nanotechnology due to their easily adjustable morphological properties and wide range of applications. Thus, a deep and systematic characterization of the morphological properties of these coatings is essential. The most important variables in the synthesis of nanoporous AAO films include the anodization voltage, nature, concentration and temperature of the electrolyte, which, combined, result in pores of different sizes and geometries. In the present work, AA 1050 alloy was used to synthesize AAO films, using 0.3 and 0.9 M oxalic acid as the electrolyte and combining different electrolyte temperatures (20, 30 and 40 °C) and anodizing voltages (30, 40 and 60 V), with the aim to correlate the morphological properties of the coatings with the synthesis parameters of a single anodization step. The coatings obtained were characterized by optical microscopy and scanning electron microscopy, determining pore diameter, interpore distance, pore density and coating thickness. The results showed that, by varying the anodic synthesis conditions, it is possible to obtain coatings with a pore diameter between 21 and 97 nm, an interpore distance between 59 and 138 nm, pore density between 2.8 × 10¹⁰ and 5.4 × 10⁹ pores/cm² and thicknesses between 15 and 145 µm. In this way, the right combination of synthesis variables allows synthesizing AAO coatings with morphological characteristics best suited to each particular application.

The influence of sol-gel dip-coating and anodic oxidation process parameters in producing thin TiO₂ films is studied. As the size of the films is in the order of nanometres (20–140 nm), to obtain a precise measurement of their thickness and analyse their crystalline structures, glancing incidence angle X-ray techniques (X-ray reflectometry and X-ray diffraction) using synchrotron radiation are used. A relationship between the colour and thickness of the films was found. This enables the film thickness to be estimated by the film colour. Within the range of the parameters studied, both techniques produce thin films with smooth surfaces which at most reproduce the roughness of the polished substrate. Independently of the technique, thermally-treated films thicker than 30 nm presented different crystalline structures with anatase and rutile phases.

The anodic oxidation of aluminium is an electrochemical technique that allows obtaining nanostructures with easily adjustable morphology depending on the synthesis variables, for its application in medicine, engineering, biotechnology, electronics, etc. In this work, low-cost aluminium oxide nanostructured films were synthesized and morphologically characterized using two anodization steps in sulphuric acid, varying the concentration and temperature of the electrolyte and anodization voltage. The order of the porous matrix, pore diameter, interpore distance, pore density, thickness, and porosity were measured and statistically analyzed. The results showed that under the proposed conditions it is possible to synthesize low-cost nanoporous aluminium oxide films, with a short-range ordering, being the best ordering conditions 10 °C and 0.3 M sulphuric acid at 20 V and 5 °C and 2 M sulphuric acid at 15 V. Furthermore, it was determined that the pore diameter and the interpore distance vary proportionally with the voltage, that the pore density decreases with the voltage and increases with the concentration of the electrolyte, and that the thickness of the oxide film increases with electrolyte concentration, temperature, and anodization voltage.

The bio- and hemocompatibility of titanium alloys are due to the formation of a TiO₂layer. This natural oxide may have fissures which are detrimental to its properties. Anodic oxidation is used to obtain thicker films. By means of this technique, at low voltages oxidation, amorphous and low roughness coatings are obtained, while, above a certain voltage, crystalline and porous coatings are obtained. According to the literature, the crystalline phases of TiO₂, anatase, and rutile would present greater biocompatibility than the amorphous phase. On the other hand, for hemocompatible applications, smooth and homogeneous surfaces are required. One way to obtain crystalline and homogeneous coatings is by heat treatments after anodic oxidation. The aim of this study is to evaluate the influence of heat treatments on the thickness, morphology, and crystalline structure of the TiO₂anodic coatings. The characterization was performed by optical and scanning electron microscopy, X-ray diffraction, and X-ray reflectometry. Coatings with different colors of interference were obtained. There were no significant changes in the surface morphology and roughness after heat treatment of 500°C. Heat treated coatings have different proportions of the crystalline phases, depending on the voltage of anodic oxidation and the temperature of the heat treatment.