Expanded thermoplastic polyurethane (ETPU) is used in a wide range of applications due to its excellent properties, but inevitably, aging deteriorates the material properties and shortens service lifetime. This study conducted aging experiments on ETPU to summarize the deterioration trend and provide reliable data. The ETPU underwent three distinct aging protocols: thermal aging for 28 days in a controlled 80 °C environment; xenon lamp aging under continuous UV irradiation (via xenon lamp) at 80 °C for 28 days; and weathering aging through 671 days of outdoor exposure to real-world weather conditions. After various structural characterization and performance tests on the aged ETPUs, the results showed that thermal aging is not the key factor causing the aging of ETPU; the internal structure of ETPU is damaged and the performance rapidly deteriorates under the combined effect of light, heat, and humidity. The special heterogeneous structure gives the sample different internal aging characteristics, and the bead interface becomes a defective site after aging, affecting the overall mechanical properties of the material. In the natural state, the lifetime of ETPU is about two years. Our work will provide valuable data for the study of the aging properties of ETPU and contribute to the prediction of the lifetime of the material.

In this paper, a novel power sintering technique, named fast hot-pressing sintering (FHP), which is able to achieve an ultrahigh heating rate similar to the spark plasma sintering (SPS) technique, but at a much lower cost, was applied to prepare a series of Al/Si composites with different Si volume ratios (12 vol.% to 70 vol.%) to meet the requirements of advanced packaging materials for electronic devices. In contrast to SPS, the FHP oven possesses a safe and budget-friendly current power supply, rather than a complex and expensive pulse power supply, for its heating power. The optimized sintering parameters (temperature, pressure and holding time) of FHP for preparing Al/Si composites were investigated and determined as 470 °C, 300 MPa and 5 min, respectively. In order to characterize the potential of Al/Si composites as packaging materials, thermal conductivities and coefficients of thermal expansion were studied. The thermal conductivity of the Al-40Si composite sintered by the FHP method is higher than that of the conventional SPS method (139 to 107 W m⁻¹ K⁻¹). With the increase in Si, the thermal conductivities and coefficients of thermal expansion on both decreases. Furthermore, the thermal conductivities obey the Agari model, whereas the coefficient of thermal expansion and Si volume ratios obey additivity. The numeric modeling would help develop required packaging materials based on the thermal performances of the substrate materials, like Si or GaAs semiconductor devices.

A novel DC-assisted fast hot-pressing (FHP) powder sintering technique was utilized to prepare Al/Diamond composites. Three series of orthogonal experiments were designed and conducted to explore the effects of sintering temperature, sintering pressure, and holding time on the thermal conductivity (TC) and sintering mechanism of an Al-50Diamond composite. Improper sintering temperatures dramatically degraded the TC, as relatively low temperatures (≤520 °C) led to the retention of a large number of pores, while higher temperatures (≥600 °C) caused unavoidable debonding cracks. Excessive pressure (≥100 MPa) induced lattice distortion and the accumulation of dislocations, whereas a prolonged holding time (≥20 min) would most likely cause the Al phase to aggregate into clusters due to surface tension. The optimal process parameters for the preparation of Al-50diamond composites by the FHP method were 560 °C-80 MPa-10 min, corresponding to a density and TC of 3.09 g cm⁻³ and 527.8 W m⁻¹ K⁻¹, respectively. Structural defects such as pores, dislocations, debonding cracks, and agglomerations within the composite strongly enhance the interfacial thermal resistance (ITR), thereby deteriorating TC performance. Considering the ITR of the binary solid-phase composite, the Hasselman–Johnson model can more accurately predict the TC of Al-50diamond composites for FHP technology under an optimal process with a 3.4% error rate (509.6 W m⁻¹ K⁻¹ to 527.8 W m⁻¹ K⁻¹). The theoretical thermal conductivity of the binary composites estimated by data modeling (Hasselman–Johnson Model, etc.) matches well with the actual thermal conductivity of the sintered samples using the FHP method.