Multicomponent oxide systems 800-Cu-Mg-Fe-O and 800-Cu-Mg-Fe-O-Ce were tested as catalysts of selective catalytic oxidation of ammonia to dinitrogen (NH₃-SCO) process. Materials were obtained by calcination of hydrotalcite-like compounds at temperature 800 °C. Some catalysts were doped with cerium by the wet impregnation method. Not only simple oxides, but also complex spinel-like phases were formed during calcination. The influence of chemical composition, especially the occurrence of spinel phases, copper loading and impregnation by cerium, were investigated. Materials were characterized by several techniques: X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), low-temperature nitrogen adsorption (BET), cyclic voltammetry (CV), temperature programmed reduction (H₂-TPR), UV-vis diffuse reflectance spectroscopy and scanning electron microscopy (SEM). Examined oxides were found to be active as catalysts of selective catalytic oxidation of ammonia with high selectivity to N₂ at temperatures above 300 °C. Catalysts with low copper amounts (up to 12 wt %) impregnated by Ce were slightly more active at lower temperatures (up to 350 °C) than non-impregnated samples. However, when an optimal amount of copper (12 wt %) was used, the presence of cerium did not affect catalytic properties. Copper overloading caused a rearrangement of present phases accompanied by the steep changes in reducibility, specific surface area, direct band gap, crystallinity, dispersion of CuO active phase and Cu²⁺ accessibility leading to the decrease in catalytic activity.

Fundamental research on direct NO decomposition is still needed for the design of a sufficiently active, stable and selective catalyst. Co-based mixed oxides promoted by alkali metals are promising catalysts for direct NO decomposition, but which parameters play the key role in NO decomposition over mixed oxide catalysts? How do applied preparation conditions affect the obtained catalyst’s properties? Co₄MnAlO_x mixed oxides promoted by potassium calcined at various conditions were tested for direct NO decomposition with the aim to determine their activity, stability and selectivity. The catalysts were prepared by co-precipitation of the corresponding nitrates and subsequently promoted by KNO₃. The catalysts were characterized by atomic absorption spectrometry (AAS)/inductive coupled plasma (ICP), X-ray photoelectron spectrometry (XPS), XRD, N₂ physisorption, temperature programmed desorption of CO₂ (TPD-CO₂), temperature programmed reduction by hydrogen (TPR-H₂), species-resolved thermal alkali desorption (SR-TAD), work function measurement and STEM. The preparation procedure affects physico-chemical properties of the catalysts, especially those that are associated with the potassium promoter presence. The addition of K is essential for catalytic activity, as it substantially affects the catalyst reducibility and basicity—key properties of a deNO catalyst. However, SR-TAD revealed that potassium migration, redistribution and volatilization are strongly dependent on the catalyst calcination temperature—higher calcination temperature leads to potassium stabilization. It also caused the formation of new phases and thus affected the main properties—S_BET, crystallinity and residual potassium amount.