Rosin is an abundantly available natural product. In this paper, for the first time, a rosin derivative is employed as the main monomer for preparation of epoxy vitrimers to improve the mechanical properties of vitrimers. Novel epoxy vitrimer networks with dynamic reversible covalent boronic ester bonds are constructed by a reaction between thiols in 2,2′–(1,4–phenylene)–bis (4–mercaptan–1,3,2–dioxaborolane) (BDB) as a curing agent and epoxy groups in the rosin derivative. The rosin-based epoxy vitrimer networks are fully characterized by Fourier transform infrared spectroscopy (FTIR), an equilibrium swelling experiment, and dynamic mechanical analysis (DMA). The obtained rosin-based epoxy vitrimers possess superior thermostability and good mechanical properties. Due to transesterification of boronic ester bonds, rosin epoxy vitrimer network topologies can be altered, giving welding, recycle, self-healing, and shape memory abilities to the fabricated polymer. Besides, the effects of treating time and temperature on welding capability is investigated, and it is found that the welding efficiency of the 20% C-FPAE sample is >93% after treatment for 12 h at 160 °C. Moreover, through a hot press, the pulverized samples of 20% C-FPAE can be reshaped several times and most mechanical properties are restored after reprocessing at 200 °C for 60 min. Finally, chemical degradation is researched for the rosin-based epoxy vitrimers.

Hydroxyl-terminated polybutadiene (HTPB)-based polyurethane (PU) networks play indispensable roles in a variety of applications; however, they cannot be reprocessed, resulting in environmental problems and unsustainable industrial development. In this work, recyclable HTPB-based PU vitrimer (HTPB-PU_V) networks are fabricated by introduction of a cross-linker 2,2′-(1,4-phenylene)-bis[4-mercaptan-1,3,2-dioxaborolane] (BDB) with dynamic boronic ester bonds into the network. Meanwhile, the BDB can stabilize the HTPB unit in the network by elimination of double bonds. The novel HTPB-PU_V networks are constructed by a thiol-ene “click” reaction and an addition reaction between HTPB and cross-linker BDB and isocyanates (HDI). The dynamic HTPB-PU_V networks are characterized by dynamic mechanical analysis (DMA) and Fourier transform infrared (FTIR). The obtained dynamic HTPB-PU_V networks possess superior thermostability. Moreover, due to the presence of dynamic boronic ester bonds, the HTPB-PU_V network topologies can be altered, contributing to the reprocessing, self-healing, and welding abilities of the final polymer. Through a hot press, the pulverized sample can be reprocessed for several cycles, and mechanical properties of the reprocessed samples are similar to those of the pristine one, with the tensile strength being even higher. The self-healed sample exhibits almost complete recovery from scratch after the healing treatment at 130 °C for 3 h. Moreover, a welding efficiency of 120% was achieved.

Thermoset polymers show favorable material properties, while bringing about environmental pollution due to non-reprocessing and unrecyclable. Diels–Alder (DA) chemistry or reversible exchange boronic ester bonds have been employed to fabricate recycled polymers with covalent adaptable networks (CANs). Herein, a novel type of CANs with multiple dynamic linkers (DA chemistry and boronic ester bonds) was firstly constructed based on a linear copolymer of styrene and furfuryl methacrylate and boronic ester crosslinker. Thermoplastic polyurethane is introduced into the CANs to give a semi Interpenetrating Polymer Networks (semi IPNs) to enhance the properties of the CANs. We describe the synthesis and dynamic properties of semi IPNs. Because of the DA reaction and transesterification of boronic ester bonds, the topologies of semi IPNs can be altered, contributing to the reprocessing, self-healing, welding, and shape memory behaviors of the produced polymer. Through a microinjection technique, the cut samples of the semi IPNs can be reshaped and mechanical properties of the recycled samples can be well-restored after being remolded at 190 °C for 5 min.

Rosin is an abundant natural product. In this paper, for the first time, a rosin derivative is employed as a monomer for the preparation of polyurethane vitrimers with improved properties. A novel rosin-based polyurethane vitrimers network was constructed by the reaction between isocyanates (HDI) as curing agent and monomers with alcohol groups modified from rosin. The dynamic rosin-based polyurethane vitrimers were characterized by FTIR and dynamic mechanical analysis. The obtained rosin-based polyurethane vitrimers possessed superior mechanical properties. Due to the dynamic urethane linkages, the network topologies of rosin-based polyurethane vitrimers could be altered, contributing self-healing and reprocessing abilities. Besides, we investigated the effects of healing time and temperature on the self-healing performance. Moreover, through a hot press, pulverized samples of 70%VPU_OH could be reshaped several times, and the mechanical properties of the recycled samples were restored, with tensile strength being even higher than the of that of the original samples.