Phenomenological plasticity models that relate relative density to plastic strain are frequently used to simulate ceramic powder compaction. With respect to the form implemented in finite element codes, they need to be modified in order to define governing parameters as functions of relative densities. Such a modification increases the number of constitutive parameters and makes their calibration a demanding task that involves a large number of experiments. The novel calibration procedure investigated in this paper is based on inverse analysis methodology, centered on the minimization of a discrepancy function that quantifies the difference between experimentally measured and numerically computed quantities. In order to capture the influence of sought parameters on measured quantities, three different geometries of die and punches are proposed, resulting from a sensitivity analysis performed using numerical simulations of the test. The formulated calibration protocol requires only data that can be collected during the compaction test and, thus, involves a relatively smaller number of experiments. The developed procedure is tested on an alumina powder mixture, used for refractory products, by making a reference to the modified Drucker–Prager Cap model. The assessed parameters are compared to reference values, obtained through more laborious destructive tests performed on green bodies, and are further used to simulate the compaction test with arbitrary geometries. Both comparisons evidenced excellent agreement.

The main hindrance to realistic models of fiber-reinforced concrete (FRC) is the local materials property variation, which does not yet reliably allow simulations at the structural level. The idea presented in this paper makes use of an existing constitutive model, but resolves the problem of localized material variation through X-ray computed tomography (CT)-based pre-processing. First, a three-point bending test of a notched beam is considered, where pre-test fiber orientations are measured using CT. A numerical model is then built with the zone subjected to progressive damage, modeled using an orthotropic damage model. To each of the finite elements within this zone, a local coordinate system is assigned, with its longitudinal direction defined by local fiber orientations. Second, the parameters of the constitutive damage model are determined through inverse analysis using load-displacement data obtained from the test. These parameters are considered to clearly explain the material behavior for any arbitrary external action and fiber orientation, for the same geometrical properties and volumetric ratio of fibers. Third, the effectiveness of the resulting model is demonstrated using a second, “control” experiment. The results of the “control” experiment analyzed in this research compare well with the model results. The ultimate strength was predicted with an error of about 6%, while the work-of-load was predicted within 4%. It demonstrates the potential of this method for accurately predicting the mechanical performance of FRC components.

This paper investigates the influence of temperature field non-uniformity on sintering simulation results using the Skorohod-Olevsky viscous sintering model. As a difference to previous studies, here a thermal transient analysis is performed to provide a detailed temperature field over the component within sintering time. Results obtained using uniform temperature distribution are compared to those obtained using a nonuniform distribution derived from a transient thermal analysis. Results are compared for different geometry sizes, that lead to different temperature non-uniformity levels. The study has shown that the temperature nonuniformity cannot always be neglected and should be considered as a possible source of modeling error.