Although chemotherapy is the most common method in clinical therapeutics with a straightforward mechanism, conventional anti-tumor drugs are still almost incapable of preventing the occurrence of tumor metastasis. In this study, we developed a multi-functional drug delivery system EINP@DOX consisting of a tea-derived polyphenol EGCG, iron ions and DOX. The system integrated the functions of tumor inhibition, diagnosis and metastasis prevention to achieve a systematic tumor treatment. The nanoscale size of EINP@DOX facilitated its accumulation in tumor tissues by means of the enhanced permeability and retention (EPR) effect, and it was then transferred to endosomes. The weakly acidic microenvironment in the endosomes of the tumor cells could destroy the coordination structure of EINP@DOX to realize the release of DOX for tumor therapy. Furthermore, the dissociative EGCG played the role of an adjuvant to restrain EMT and down-regulate the MMP levels, which could prevent the occurrence of tumor metastasis. Meanwhile, iron ions as superior magnetic resonance imaging (MRI) contrast agents provided visual evidence for the accurate location of EINP@DOX. In vitro and in vivo studies demonstrated that EINP@DOX showed a remarkable performance in tumor diagnosis and excellent therapeutic efficacy, inhibiting the metastasis of tumor cells effectively at the same time.

During mechanical processes, violent friction and wear between the friction contact surfaces not only causes wear to mechanical components, reducing the instrument life, but also causes friction heat, reducing the working efficiency of machines during operation. The addition of graphene-reinforced grease to the mechanical friction surface can effectively reduce the friction coefficient and improve the thermal conductivity. In this work, the tribological properties and thermal conductivity of base grease with graphene were investigated systematically. The tribological results showed that the grease with 2 wt% graphene had the best tribological properties among all these greases. The wear scar diameter and average friction coefficient of graphene grease with 2 wt% graphene reached 0.43 mm and 0.10 (the values for base grease are 0.50 mm and 0.118), respectively. In addition, the average friction coefficient and wear scar diameter increased proportionally with the increasing load and frequency. The thermal conductivity of the grease with 4 wt% graphene reached 0.28 W (m K)⁻¹, an increase of 55.5% in comparison with the base grease. It is proposed that the addition of graphene into the base grease effectively enhanced the tribological properties and thermal conductivity.

3D Printed biodegradable polymeric scaffolds are critical to repair a bone defect, which can provide the individual porous and network microenvironments for cell attachment and bone tissue regeneration. Biodegradable PCL/HA composites were prepared with the blending of poly(ε-caprolactone) (PCL) and hydroxyapatite nanoparticles (HA). Subsequently, the PCL/HA scaffolds were produced by the melting deposition-forming method using PCL/HA composites as the raw materials in this work. Through a serial of in vitro assessments, it was found that the PCL/HA composites possessed good biodegradability, low cell cytotoxicity, and good biocompatibility, which can improve the cell proliferation of osteoblast cells MC3T3-E1. Meanwhile, in vivo experiments were carried out for the rats with skull defects and rabbits with bone defects. It was observed that the PCL/HA scaffolds allowed the adhesion and penetration of bone cells, which enabled the growth of bone cells and bone tissue regeneration. With a composite design to load an anticancer drug (doxorubicin, DOX) and achieve sustained drug release performance, the multifunctional 3D printed PCL/HA/DOX scaffolds can enhance bone repair and be expected to inhibit probably the tumor cells after malignant bone tumor resection. Therefore, this work signifies that PCL/HA composites can be used as the potential biodegradable scaffolds for bone repairing.

Biodegradable scaffolds based on biomedical polymeric materials have attracted wide interest in bone transplantation for clinical treatment for bone defects without a second operation. The composite materials of poly(trimethylene carbonate), poly(L-lactic acid), and hydroxyapatite (PTMC/PLA/HA and PTMC/HA) were prepared by the modification and blending of PTMC with PLA and HA, respectively. The PTMC/PLA/HA and PTMC/HA scaffolds were further prepared by additive manufacturing using the biological 3D printing method using the PTMC/PLA/HA and PTMC/HA composite materials, respectively. These scaffolds were also characterized by Fourier transform infrared spectroscopy (FT-IR), gel permeation chromatography (GPC), automatic contact-angle, scanning electronic micrographs (SEM), diffraction of X-rays (XRD), differential scanning calorimetry (DSC), and thermogravimetry (TG). Subsequently, their properties, such as mechanical, biodegradation, cell cytotoxicity, cell compatibility in vitro, and proliferation/differentiation assay in vivo, were also investigated. Experiment results indicated that PTMC/PLA/HA and PTMC/HA scaffolds possessed low toxicity, good biodegradability, and good biocompatibility and then enhanced the cell multiplication ability of osteoblast cells (MC3T3-E1). Moreover, PTMC/PLA/HA and PTMC/HA scaffolds enhanced the adhesion and proliferation of MC3T3-E1 cells and enabled the bone cell proliferation and induction of bone tissue formation. Therefore, these composite materials can be used as potential biomaterials for bone repatriation and tissue engineering.