Wood in the cold temperate zone is the product of the alternation of the growing season and the dormant period of trees, but our knowledge of the process of dormancy release in trees remains limited. Chinese fir (Cuninghamia lanceolata (Lamb.) Hook.) was used to investigate cellular and metabolite changes in the secondary phloem tissue during dormancy release. The sampling dates were 2 March, 28 March, and 13 April. The microsections of wood-forming tissue were prepared using the paraffin embedding technique to observe the formation of cambium cells; metabolites in secondary phloem cells were extracted using a methanol/chloroform organic solvent system. The results showed that the secondary phloem consists of phloem fibers, sieve cells and phloem parenchyma. The cells were regularly arranged in continuous tangential bands and were in the order of Phloem fiber-Sieve cell-Phloem parenchyma-Sieve cell-Phloem parenchyma-Sieve cell-Phloem parenchyma-Sieve cell-Sieve cell-Phloem parenchyma-. The Chinese fir cambium was in dormancy on 2 March and 28 March, while on 13 April, it was already in the active stage and two layers of xylem cells with several layers of phloem cells were newly formed. The width of the cambium zone increased from 18.7 ± 5.7 μm to 76.5 ± 3.0 μm and the average radial diameter of sieve cells expanded from 15.4 ± 7.5 μm to 21.5 ± 7.4 μm after dormancy release. The cambium zone width and the average radial diameter of sieve cells before and after dormancy release were significantly different (p < 0.01). The phloem parenchyma cells without resin were squeezed and deformed by the sieve cells, and the width of the phloem during the active period was 197.0 ± 8.5 μm, which was larger than that during the dormant period. Ultra-performance liquid chromatography-tandem mass spectrometry (UPLC-MS/MS)-based metabolomics was employed to analyze the secondary phloem of Chinese fir on 28 March and 13 April. Thirty-nine differential metabolites during dormancy release were detected. The results showed that the composition of Chinese fir metabolites was different before and after dormancy release. The relative increase in pyruvic acid and ascorbic acid contents proved that the rate of energy metabolism in Chinese fir increased substantially after dormancy release. Changes in cell development and the composition of metabolites revealed that the dormancy release of Chinese fir was at early April and the formation period of phloem tissue is earlier than xylem tissue.

The Taxodium hybrid Zhongshanshan fast-growing species is susceptible to environment and gravity to form reaction wood. In this study, individual growth rings of reaction wood are used as subjects, and an individual growth ring is divided into three zones: compression zone (CZ), lateral zone (LZ), and opposite zone (OZ). The microanatomical structure and chemical properties of the tracheids in CZ, LZ, and OZ forms by the inclined or bent growth of T. Zhongshanshan are comparatively analyzed by using optical microscopy, scanning electron microscope, laser confocal microscopy, and Raman imaging techniques. In CZ, the length and diameter of compression wood (CW) tracheids decreased, and the shape of cross-sections became rounded as compared to the OZ and LZ tracheids. More notably, threaded fissures appeared on the cell wall of tracheids, and the thickness of the cell wall increased in CW. The analysis of tracheids’ cell wall structure showed that CW tracheids had a complete outer secondary wall middle (S2L) layer, but had no secondary wall inner (S3) layer. In the transition zone (TA) between CW and normal early wood, tracheids were divided into compressed and normal tracheids. Despite the compressed tracheids having a similar cell morphology to normal tracheids, they had a thin secondary wall S2L layer. Tracheids in LZ had a thin S2L layer only at the angle of the cell. No S2L layer was seen in the cell wall of OZ and CZ late wood tracheids. It can be concluded that the response of lignin deposition location to external stress was faster than the change in cell morphology. The above results help provide the theoretical basis for the response mechanism of T. Zhongshanshan reaction wood anatomical structures to the external environment and has important theoretical value for understanding its characteristics and its rational and efficient usage.

The thermal conductivity and the deformation of wood from the Taxodium hybrid ‘Zhongshanshan’ were studied in the process of heat transfer. The results showed that the average thermal conductivity of this wood was 0.1257 W/(m·K) under the condition of 12% wood moisture content and 30 °C heat transfer temperature. When the testing temperature exceeded 0 °C, the thermal conductivity increased linearly with both temperature and wood moisture content and was affected by the moisture content of the wood. During the heat transfer process, the deformation of features caused repeated swelling and shrinkage in the longitudinal, radial, and tangential directions. The dimensional change was greatly affected by the wood’s moisture content and was less affected by the temperature. These results are of great meaning for the study of the heat transfer process of Taxodium hybrid ‘Zhongshanshan’ wood. Furthermore, it provides a scientific basis for the heat preservation effect, drying treatment, and pyrolysis treatment of Taxodium hybrid ‘Zhongshanshan’ wood for use as a building material.