Triboelectric nanogenerators (TENGs) have revealed widespread success in converting ambient mechanical energy into electric power. However, the challenge remains to improve the output performance for extensive applications. Herein, a strategy of combining surface texturing and dielectric constant control is developed to enhance the output performance of poly-dimethylsiloxane (PDMS)-based TENGs. The introduction of highly dielectric particles significantly enhanced the dielectric constant and surface charge potential of the PDMS film, supported by both experimental analysis and COMSOL simulation. With an optimized weight ratio, an output voltage of ∼390 V (peak to peak), a short-circuit current density of ∼170 mA m⁻², and a charge density of ∼108 μC m⁻² were obtained, corresponding to the peak power density of 9.6 W m⁻², showing a 10-fold power improvement compared with flat PDMS-based TENGs. This work demonstrates a promising strategy for exploring high performance triboelectric generators.

Radiative cooling can make the selective emitter cool below ambient temperature without any external energy. Recent advances in photonic crystal and metamaterial technology made a high-efficiency selective emitter achievable by precisely controlling the emitter’s Infrared emission spectrum. However, the high cost of the photonic crystals and meta-materials limit their application. Herein, an efficient bilayer selective emitter is prepared based on the molecular vibrations of functional nanoparticles. By optimizing the volume fraction of the functional nanoparticles, the bilayer selective emitter can theoretically cool 36.7 °C and 25.5 °C below the ambient temperature in the nighttime and daytime, respectively. Such an efficient cooling performance is comparable with the published photonic crystal and metamaterial selective emitters. The rooftop measurements show that the bilayer selective emitter is effective in the ambient air even under direct sunlight. The relatively low cost and excellent cooling performance enable the bilayer selective emitter to have great potential for a practical purpose.

Tobermorite and Al-substituted tobermorite with varying Al/(Si + Al) molar ratios were synthesized via the static hydrothermal method. The effect of different Al substitution ratios on the structure of tobermorite was investigated by XRD, SEM–EDS, TG–DSC, FT–IR, ²⁹Si, and ²⁷Al MAS–NMR. The interplanar crystal spacing of (002) increased with the increment of the Al substitution ratio. The maximum ratio of the Al substitution for Si in the structure of tobermorite was about 15 at %, which was limited by the compositions of tobermorite and the electrostatic repulsive forces caused by Al substitution. The DSC curve of the tobermorite with an Al/(Al + Si) molar ratio of 0.15 showed a larger exothermic peak area at 850 °C, indicating that the Al-O-Si bond was formed in the structure of tobermorite and the Al participated in the recrystallization. The ²⁹Si and ²⁷Al MAS–NMR results confirmed that tetrahedral Al was introduced into the structure of the tobermorite. New silicon sites, Q²(1Al) and Q³(1Al), formed by the Al substitution for Si in bridging and non-bridging sites, were detected. Compared to the tobermorite without Al substitution, the adsorption capacity of Al-substituted tobermorite with Al/(Al + Si) = 0.15 to Na⁺ was improved by 44%.

Radiative cooling is a passive cooling technology that can cool a space without any external energy by reflecting sunlight and radiating heat to the universe. Current reported radiative cooling techniques can present good outside test results, however, manufacturing an efficient radiative material which can be applied to the market for large-scale application is still a huge challenge. Here, an effective radiative cooling coating with a near-ideal selective emissive spectrum is prepared based on the molecular vibrations of SiO_x, mica, rare earth silicate, and molybdate functional nanoparticles. The radiative cooling coating can theoretically cool 45 °C below the ambient temperature in the nighttime. Polyethylene terephthalate (PET) aluminized film was selected as the coating substrate for its flexibility, low cost, and extensive production. As opposed to the usual investigations that measure the substrate temperature, the radiative cooling coating was made into a cubic box to test its space cooling performance on a rooftop. Results showed that a temperature reduction of 4 ± 0.5 °C was obtained in the nighttime and 1 ± 0.2 °C was achieved in the daytime. Furthermore, the radiative cooling coating is resistant to weathering, fouling, and ultraviolet radiation, and is capable of self-cleaning due to its hydrophobicity. This practical coating may have a significant impact on global energy consumption.