China faces the problem of depletion of its coal resources, and a large number of mines are becoming aged mines. Demand for coal, however, still increases due to the growth of China’s economy. Energy shortage might restrict the sustainability of China’s national economy. As one contribution to a solution, this paper proposes the innovative exploitation method of solid backfill coal mining (SBCM) technology to exploit parts of pillar-blocked (residual coal pillar resources under industrial square, RCPRIS) that protect industrial facilities. Thus, blocked coal resources may be converted into mineable reserves that improve the recovery ratio of mine resources. Also, waste would be removed from the surface reducing hazards of environmental pollution. Based on the case of the Baishan Coal Mine in Anhui, China, numerical simulation is used to study the size of shaft-protecting coal pillars (SPCP) required at different backfill ratios. Results show that the disturbance to a shaft caused by exploitation decreases with the increase of the backfill ratio. When using SBCM to exploit RCPRIS under the condition of 80% backfill ratio, compared with the caving method, a lot of pillar-blocked coal resources would be freed. The life of Baishan Coal Mine would be prolonged, resulting in appreciable social, environmental, and economic benefits.

Asphalt is a widely used polymeric material in pavement engineering. However, it is easily affected by heat and ultraviolet rays, which accelerate its molecular degradation and physicochemical aging, thereby limiting its service life. To improve the anti-aging properties of asphalt, three types of nano-zinc oxide (ZnO)-modified asphalt were prepared. The chemo-rheological behavior, structural evolution of polymeric components, molecular weight distribution, and nanoscale morphology of nano-ZnO-modified asphalt were studied via dynamic shear rheometry (DSR), Fourier transform infrared spectrometry (FTIR), gel permeation chromatography (GPC) and atomic force microscopy (AFM), and the aging resistance of nano-ZnO-modified asphalt was quantitatively analyzed using the rutting factor index, functional group index, molecular size ratio, and nanoscale parameters. The findings indicate that nano-ZnO enhances the high-temperature rheological properties of asphalt and delays the increase in the rutting factor of aged asphalt. Nano-ZnO is dispersed in the asphalt matrix in the form of a physical mixture without inducing new chemical bonds, and can reduce the nanoscale roughness of asphalt. After aging, the nanoscale roughness and the aspect ratio of the bee structure decreased, and the bee structure area increased. According to the changes in the functional group index and the proportions of molecular sizes in the asphalt, it was found that nano-ZnO can significantly improve asphalt’s aging resistance. The results of this study provide insights into the nanoscale modification and structure–property relationships of polymeric asphalt binders, providing a reference for the design and application of functional polymer nanocomposite systems with improved durability.

Geological hazards, such as the frequent occurrence of rock bursts in deep mining, emphasize the critical necessity for the early warning and prediction of dynamic fractures in coal and rock masses, as well as the destabilization of the surrounding rock. This study delves into the mechanisms of electromagnetic radiation (EMR) signals and their synchronous coupling with micro-seismic (ME) signals. EMR and ME signals from rock specimens were systematically collected during the uniaxial compression fracture process using a dedicated monitoring and acquisition system. Employing the wavelet analysis method, the original data underwent reconstruction and denoising, while the EMR and ME spectra, derived through fast Fourier transform, were subjected to detailed scrutiny. The comprehensive analysis unveiled that EMR signals arising from rock fractures exhibited precise timing synchronization with ME signals. Moreover, the dominant frequencies of both signals are closely aligned within the low-frequency band, indicating a remarkable degree of similarity and homology. These findings establish an experimental basis for the development of monitoring and early warning systems geared toward assessing damage to coal and rock masses using EMR and ME signals.

To study the flow and strength characteristics of loess-based backfill materials, orthogonal tests were used to design a cemented backfill material combining loess, high-water content materials, cement, and fly ash. By using the range, analysis of variance, and multi-variate regression analysis, influences of four key factors on the initial setting time, diffusivity, compressive strength, and shear strength of the backfill material were investigated. These four factors included the mass concentration of loess water (A), the content of high-water content materials (B), cement content (C), and content of fly ash (D). The results showed that the initial setting time, diffusivity, compressive strength, and shear strength of the backfill material were 13~33 min, 400~580 mm, 0.917–3.605 MPa, and 0.360–0.722 MPa, respectively, all distributed in wide ranges. For the initial setting time, the four factors were listed in descending order as A > D > B > C according to their influences; for diffusivity, the four factors were listed as A > B > C > D; for the compressive strength, the four factors were ranked as A > C > D > B; for the shear strength, the four factors were ranked such that A > C > D > B. With regard to the comprehensive index, the four factors were such that A > B > D > C. That is, the factors were listed in descending order as the mass concentration of loess water, cement content, the content of fly ash, and content of high-water content materials according to their significance in influencing characteristics of the loess-based backfill material. Comprehensive analysis indicated that the fluidity of the material was mainly influenced by the mass concentration of loess water, and the two were negatively correlated. The hydro-consolidation effect of materials with high-water contents accelerated material solidification. The strength of the backfill material was mainly influenced by the cement content while only slightly affected by contents of other materials. In this way, a prediction model for characteristic parameters, namely, fluidity and strength, of the loess-based backfill material under the action of various factors was established.

To study the influences of different mix proportions of materials on the ultrasonic p-wave velocity of coal slime based backfill materials, influences of four factors on the p-wave velocity of specimens were investigated by designing orthogonal tests and taking coal slime as the principal raw material. The four factors included the following: (A) the mass concentration of coal slime, (B) the content of high-water-content material, (C) cement content, (D) and content of fly ash. Test results revealed the following: (1) the ultrasonic p-wave velocity is in the range of 3.916 to 8.319 km/s and various factors are listed in a descending order as A, D, B, and C according to their influences on the ultrasonic p-wave velocity; (2) the ultrasonic p-wave velocity is positively correlated with the compressive strength and shear strength, with correlation coefficients separately of 0.87 and 0.65; (3) the equations for variations in the ultrasonic p-wave velocity under influences of different factors are fitted. The ultrasonic p-wave velocity has a quadratic polynomial relationship with factor A, while following exponential relationships with factors B, C, and D. A predictive model for characteristic parameters of the ultrasonic p-wave velocity of coal slime based backfill materials jointly influenced by the four factors was established based on the fitting equation for variations of single factors and ultrasonic p-wave velocity. The predictive model was then verified.