Today, more disciplines are intercepting each other, giving rise to “cross-disciplinary” research. Technological advancements in material science and device structure and production have paved the way towards development of new classes of multi-purpose sensory devices. Organic phototransistors (OPTs) are photo-activated sensors based on organic field-effect transistors that convert incident light signals into electrical signals. The organic semiconductor (OSC) layer and three-electrode structure of an OPT offer great advantages for light detection compared to conventional photodetectors and photodiodes, due to their signal amplification and noise reduction characteristics. Solution processing of the active layer enables mass production of OPT devices at significantly reduced cost. The chemical structure of OSCs can be modified accordingly to fulfil detection at various wavelengths for different purposes. Organic phototransistors have attracted substantial interest in a variety of fields, namely biomedical, medical diagnostics, healthcare, energy, security, and environmental monitoring. Lightweight and mechanically flexible and wearable OPTs are suitable alternatives not only at clinical levels but also for point-of-care and home-assisted usage. In this review, we aim to explain different types, working mechanism and figures of merit of organic phototransistors and highlight the recent advances from the literature on development and implementation of OPTs for a broad range of research and real-life applications.

Green synthesis of graphene from graphite was carried out in molten salt mixture of LiCl-KCl, which is an environmentally friendly alternative to traditional methods using a large number of chemicals. The effect of carbonization temperature on the final properties of graphene products was investigated at a temperature range of 500-800°C. The layer numbers of graphene products were determined as a single layer and few layers by XRD and Raman analyses. The highest conductivity value of 1219 S/m was reached with the sample synthesized at 600°C (GGr600), which is 10-fold higher than that of commercial graphene (CG) (115 S/m). The percentage of carbon contents of GGr600 and sample synthesized at 800°C (GGr800) was determined as 86% and 73% by XPS. From the SEM analyses, it was observed that graphene products have sheet-like structures. A TEM image showed that GGr800 has the thickness changing from 5-9 nm, pointing out the graphene with few layers. AFM analysis demonstrated that GGr600 has a single-layer sheet-like structure.

The liquid-phase exfoliation (LPE) method has been gaining increasing interest by academic and industrial researchers due to its simplicity, low cost, and scalability. High-intensity ultrasound energy was exploited to transform graphite to graphene in the solvents of dimethyl sulfoxide (DMSO), N,N-dimethyl formamide (DMF), and perchloric acid (PA) without adding any surfactants or ionic liquids. The crystal structure, number of layers, particle size, and morphology of the synthesized graphene samples were characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), ultraviolet visible (UV–vis) spectroscopy, dynamic light scattering (DLS), and transmission electron microscopy (TEM). XRD and AFM analyses indicated that G-DMSO and G-DMF have few layers while G-PA has multilayers. The layer numbers of G-DMSO, G-DMF, and G-PA were determined as 9, 10, and 21, respectively. By DLS analysis, the particle sizes, polydispersity index (PDI), and zeta potential of graphene samples were estimated in a few micrometers. TEM analyses showed that G-DMSO and G-DMF possess sheet-like fewer layers and also, G-PA has wrinkled and unordered multilayers.

This study presents an easy and quick method for the synthesis of graphene from graphite in a set of solvents, including n-Hexadecane (n-Hexa), dimethylsulfoxide (DMSO), sodium hydroxide (NaOH), 1-octanol (OCTA), perchloric acid (PA), N,N-Dimethylformamide (DMF), ethylene glycol (EG), and ethylene diamine (ED), via microwave (MW) energy. The properties of final products were determined by X-ray diffraction spectroscopy (XRD), Fourier transform infrared spectroscopy (FTIR), ultraviolet-visible (UV-Vis) spectroscopy, and the four-point probe technique. The XRD spectra of most of the MW-assisted graphene products showed peaks at 2θ = 26.5° and 54°. Layer numbers extend from 2 and 25, and the leading comes about were gotten by having two-layered products, named as graphene synthesized in dimethylsulfoxide (G-DMSO), graphene synthesized in ethylene glycol (G-EG), and graphene synthesized in 1-octanol (G-OCTA). G-DMF has the highest electrical conductivity with 22 S/m. The electrical conductivity is higher when the dipole moment of the used solvent is between 2 and 4 Debye (D). The FTIR spectra of most of the MW-assisted graphene products are in line with commercial graphene (CG). The UV-Vis spectra of all MW-assisted graphene products showed a peak at 223 nm referring to characteristic sp2 C=C bonds and 273 nm relating to the n → π * transition of C-O bonds.

Liquid Phase Exfoliation (LPE) method has been gaining increasing interest by academic and industrial researchers due to its simplicity, low-cost, and scalability. High intensity ultrasound energy was exploited to transform graphite to graphene in the solvents of dimethyl sulfoxide (DMSO), N,N-dimethyl formamide (DMF), and perchloric acid (PA) without any surfactants or ionic liquids. The crystal structure, number of layers, particle size, and morphology of the synthesized graphene samples were characterized by X-ray Diffraction (XRD), Atomic Force Microscopy (AFM), Ultraviolet visible (UV–vis) spectroscopy, Dynamic Light Scattering (DLS), and Transmission Electron Microscopy (TEM). XRD and AFM analyses indicated that G-DMSO and G-DMF have few layers and G-PA has multilayers. The layer numbers of G-DMSO, G-DMF, and G-PA were determined as 9, 10, and 21, respectively. By DLS analysis, the particle sizes of graphene samples were estimated in a few micrometers. TEM analyses showed that G-DMSO and G-DMF possess sheet-like fewer layers and also, G-PA has wrinkled and unordered multilayers.