Titanium dioxide (TiO2) nanotube arrays coupled with a narrow gap semiconductor—bismuth selenide (Bi2Se3)—exhibited remarkable enhancement in the photocathodic protection property for 304 stainless steel under visible light. Bi2Se3/TiO2 nanocomposites were successfully synthesized using a simple two-step method, including an electrochemical anodization method for preparing pure TiO2 and a chemical bath deposition method for synthesizing Bi2Se3 nanoflowers. The morphology and structure of the composite films were studied by scanning electron microscopy, energy dispersion spectroscopy, X-ray photoelectron spectroscopy and X-ray diffraction. In addition, the influence of the Bi2Se3 content on the photoelectrochemical and photocathodic protection properties of the composite films was also studied. The photocurrent density of the Bi2Se3/TiO2 nanocomposites was significantly higher than that of pure TiO2 under visible light. The sensitizer Bi2Se3 enhanced the efficient separation of the photogenerated electron-hole pairs and the photocathodic protection properties of TiO2. Under visible light illumination, Bi2Se3/TiO2 nanocomposites synthesized by the chemical bath deposition method with Bi3+ (0.5 mmol/L) exhibited the optimal photogenerated cathodic protection performance for 304 stainless steel.

The container of high-level radioactive waste (HLRW) being in deep geological disposal, the backfill material is needed to serve as the second defense for HLRW and the highly compacted bentonite is generally selected. As the time goes, the underground water will infiltrate the backfill, causing the corrosion of materials for the building of containers in the formed electrolyte. Carbon steel, titanium and its alloy are the potential candidate materials for the fabrication of HLRW containers. The current investigation aims at assessing the safety of HLRW container in deep geological disposal for hundreds of thousands of years and facilitating the material selection for future container fabrication by estimating their corrosion behavior in compacted bentonite with a series of moisture content at different temperatures through electrochemical methods including open circuit potential (OCP), electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curve (PC) measurements. The corrosion rates were estimated for a carbon steel, a pure titanium and a titanium alloy in compacted Gaomiaozi Bentonite infiltrated with simulated underground water in Beishan area of China over an expected disposal period up to 10⁶ years respectively, showing that titanium and its alloy are more reliable materials for building HLRW containers than carbon steel.

High-strength steels are widely used in marine engineering; however, they suffer from the risks of corrosion, hydrogen permeation, and stress corrosion cracking (SCC) in wet–dry cyclic marine environments. In this study, the corrosion, hydrogen permeation, and SCC behaviours of AISI 4135 steel in the tidal zone were investigated using electrochemical corrosion, electrochemical hydrogen permeation, and slow strain rate tests, respectively, via field exposure. The results showed that the AISI 4135 steel sample placed at the high tide level had high SCC susceptibility because of severe pitting corrosion and hydrogen permeation, whereas the steel samples placed at the middle and low tide levels had low SCC susceptibilities. The dry/wet time ratio was crucial in determining the SCC behaviour and mechanism of the steel in the tidal zone. With increasing time ratio, the SCC mechanism changed from micro-void coalescence control to localised anodic dissolution and hydrogen embrittlement in tandem.