The flexible tactile sensor has attracted widespread attention because of its great flexibility, high sensitivity, and large workable range. It can be integrated into clothing, electronic skin, or mounted on to human skin. Various nanostructured materials and nanocomposites with high flexibility and electrical performance have been widely utilized as functional materials in flexible tactile sensors. Polymer nanomaterials, representing the most promising materials, especially polyvinylidene fluoride (PVDF), PVDF co-polymer and their nanocomposites with ultra-sensitivity, high deformability, outstanding chemical resistance, high thermal stability and low permittivity, can meet the flexibility requirements for dynamic tactile sensing in wearable electronics. Electrospinning has been recognized as an excellent straightforward and versatile technique for preparing nanofiber materials. This review will present a brief overview of the recent advances in PVDF nanofibers by electrospinning for flexible tactile sensor applications. PVDF, PVDF co-polymers and their nanocomposites have been successfully formed as ultrafine nanofibers, even as randomly oriented PVDF nanofibers by electrospinning. These nanofibers used as the functional layers in flexible tactile sensors have been reviewed briefly in this paper. The β-phase content, which is the strongest polar moment contributing to piezoelectric properties among all the crystalline phases of PVDF, can be improved by adjusting the technical parameters in electrospun PVDF process. The piezoelectric properties and the sensibility for the pressure sensor are improved greatly when the PVDF fibers become more oriented. The tactile performance of PVDF composite nanofibers can be further promoted by doping with nanofillers and nanoclay. Electrospun P(VDF-TrFE) nanofiber mats used for the 3D pressure sensor achieved excellent sensitivity, even at 0.1 Pa. The most significant enhancement is that the aligned electrospun core-shell P(VDF-TrFE) nanofibers exhibited almost 40 times higher sensitivity than that of pressure sensor based on thin-film PVDF.

A comprehensive review on designs and mechanisms of ZnO-based NO₂ gas sensors operated at low temperature.

The discovery of low‐cost and high‐performance bifunctional oxygen electrocatalysts is vital to the future commercialization of rechargeable zinc‐air batteries (ZABs). Herein, a Fe single atom seed‐mediated strategy is reported for the fabrication of Fe₃C species closely surrounded by FeN₄C active sites with strong electronic interactions built between them and more importantly, creating optimized coordination environment, via subtly adjusting their ratio, for favorable adsorption energies of oxygen intermediates formed during oxygen reduction reaction (ORR) and oxygen evolution reaction (OER). Concretely, the voltage difference (ΔE) between the ORR half‐wave and OER potential at a current density of 10 mA cm⁻² for the compositionally‐optimized FeNC/Fe₃C‐op electrocatalyst is only 0.668 V, endowing itself one of the best bifunctional OER/ORR benchmarks. As a demo, ZABs assembled with FeNC/Fe₃C‐op as the air cathode deliver a remarkable specific capacity (818.1 mAh g_Zn⁻¹) and a power density (1013.9 mWh g_Zn⁻¹), along with excellent long‐term durability (>450 h). This work extends the methodology to modulate the activity of FeN₄C atomic site, undoubtedly inspiring wide explorations on the precise design of bifunctional oxygen electrocatalysts.

Zinc oxide (ZnO) nanoparticles modified with uniformly dispersed silver (Ag) nanoparticles (Ag-ZnO) were prepared in one step by calcining precursor electrospun nanofibers. The molar ratios of Ag to Zn in the precursor solutions were 0, 1, 3, and 5%. The microstructure of the Ag-ZnO sensor was characterized by scanning electron microscopy and transmission electron microscopy. The existence of metallic Ag was confirmed by X-ray diffraction and X-ray photoelectron spectroscopy, and the gas sensing properties of Ag-ZnO were investigated. The results showed that the ZnO nanoparticles after Ag nanoparticles modification exhibited excellent gas sensing performance to ethanol and hydrogen sulfide (H₂S). The optimal working temperature of the Ag-ZnO sensor significantly decreased for ethanol compared with pure ZnO. The 3% Ag-ZnO sensor exhibited the fastest response to ethanol with the response/recovery times of only 5 and 9 s, respectively. However, all the Ag-ZnO-based gas sensors showed a high response value to H₂S, especially the 3% Ag-ZnO gas sensor exhibited a maximum response value of 298 at 10 ppm H₂S. These results could be attributed to the spillover effect and electron sensitization effect of Ag nanoparticles, which led to more absorbed oxygen species and active sites, and thereby can further enhance the gas sensing performances of ZnO-based gas sensors.