Utilization of biomass either as a renewable energy source or for the generation of biogenic materials has received considerable interest during the past years. In the case of rice husk (RH) and rice straw (RS) with high silica contents in the fuel ash, these approaches can be combined to produce high-grade biogenic silica with purities >98 wt % from combustion residues. The overall process can be considered nearly neutral in terms of CO₂ emission and global warming, but it can also address disposal challenges of rice husk and rice straw. For the resulting biogenic silica, several advanced application opportunities exist, e.g., as adsorbents, catalysts, drug delivery systems, etc. This article provides a comprehensive literature review on rice husk and rice straw combustion as well as applied strategies for raw material pre-treatment and/or post-treatment of resulting ashes to obtain high quality biogenic silica. Purity of up to 97.2 wt % SiO₂ can be reached by combustion of untreated material. With appropriate fuel pre-treatment and ash post-treatment, biogenic silica with purity up to 99.7 wt % can be achieved. Studies were performed almost exclusively at a laboratory scale.

Increased amounts of available biomass residues from agricultural food production are present widely around the globe. These biomass residues can find essential applications as bioenergy feedstock and precursors to produce value-added materials. This study assessed the production of biogenic silica (SiO₂) from different biomass residues in Africa, including cornhusk, corncob, yam peelings, cassava peelings and coconut husks. Two processes were performed to synthesize the biogenic silica. First, the biomass fuels were chemically pre-treated with 1 and 5% w/v citric acid solutions. In the second stage, combustion at 600 °C for 2 h in a muffle oven was applied. The characterization of the untreated biomasses was conducted using Inductively coupled plasma—optical emission spectrometry (ICP-OES), thermal analysis (TG-DTA) and Fourier-transform infrared spectroscopy (FTIR). The resulting ashes from the combustion step were subjected to ICP, nitrogen physisorption, Energy dispersive X-ray spectroscopy (EDX) as well as X-ray diffraction (XRD). ICP results revealed that the SiO₂ content in the ashes varies between 42.2 to 81.5 wt.% db and 53.4 to 90.8 wt.% db after acidic pre-treatment with 1 and 5 w/v% acid, respectively. The relative reductions of K₂O by the citric acid in yam peel was the lowest (79 wt.% db) in comparison to 92, 97, 98 and 97 wt.% db calculated for corncob, cassava peel, coconut husk and cornhusk, respectively. XRD analysis revealed dominant crystalline phases of arcanite (K₂SO₄), sylvite (KCl) and calcite (CaCO₃) in ashes of the biomass fuels pre-treated with 1 w/v% citric acid due to potassium and calcium ions present. In comparison, the 5 w/v% citric acid pre-treatment produced amorphous, biogenic silica with specific surface areas of up to 91 m²/g and pore volumes up to 0.21 cm³/g. The examined biomass residues are common wastes from food production in Africa without competition in usage with focus application. Our studies have highlighted a significant end-value to these wastes by the extraction of high quality, amorphous silica, which can be considered in applications such as catalyst support, construction material, concrete and backing material.

In order to assess the possibility of silica production via smoldering of moist rice husk, experiments of washed (moist) rice husk (7 kg with moisture content of 51%) in a newly designed smoldering apparatus was performed. The temperature inside the fuel bed during smoldering was recorded, and characteristics of ash were analyzed. Results showed that the highest temperature in the middle of the naturally piled fuel bed was about 560.0 °C, lower than those in most of combustors. Some volatiles from the lower part of the fuel bed adhere to its upper ash during piled smoldering. Silica content and specific surface area of ash from smoldering of washed (moist) rice husk were 86.4% and 84.9 m²/g, respectively. Compared to our experiments, they are close to smoldering of unwashed rice husk (89.0%, 67.7 m²/g); different from muffle furnace burning (600 °C, 2 h) of washed (93.4%, 164.9 m²/g) and un-washed (90.2%, 45.7 m²/g) rice husk. The specific surface area is higher than those from most industrial methods (from 11.4 to 39.3 m²/g). After some improvements, the smoldering process has great potential in mass product of high quality silica directly from moist rice husk.

This paper presents the results of adsorption and permeation experiments of hydrogen and methane at elevated temperatures on a carbon-based nanoporous membrane material provided by Fraunhofer IKTS. The adsorption of pure components was measured between 90 °C and 120°C and pressures up to 45 bar. The Langmuir adsorption isotherm shows the best fit for all data points. Compared to available adsorption isotherms of H₂ and CH₄ on carbon, the adsorption on the investigated nanoporous carbon structures is significantly lower. Single-component permeation experiments were conducted on membranes at temperatures up to 220 °C. After combining the experimental results with a Maxwell–Stefan surface diffusion model, Maxwell–Stefan surface diffusion coefficients ${\mathcal{D}}_i^s$ were calculated. The calculated values are in line with an empirical model and thus can be used in future multi-component modeling approaches in order to better analyze and design a membrane system. The published adsorption data fill a gap in the available adsorption data for CH₄ and H₂.