Steel fibers change the properties of hardened concrete significantly. However, addition of fibers to fresh concrete results in a loss of workability. Self-compacting concrete (SCC) is an innovativ...

We cover teeth surfaces with nanohybrid coatings containing an inorganic ceramic and an organic copolymer constituents. We report the first ever values of scratch penetration depth and scratch recovery for bare and coated teeth. We find that uncoated teeth undergo viscoelastic recovery (healing) after microscratching—the first manifestation of bone viscoelasticity in tribology. The coatings fill “valleys” in teeth surfaces. In each case a large improvement in the scratch resistance as compared to uncoated teeth is seen. The extent of the improvement depends on the inorganic/organic component ratios in the nanohybrids.

Samples were prepared by addition of a fluorinated poly(aryl ether ketone) (12F-PEK) to a commercial epoxy resin and curing at either 24 °C or 70 °C. The concentrations of fluoropolymer in the samples were 0, 5, 10, 20, 30, 40, and 50%. Phase inversion facilitates the formation of more and more smooth surfaces for scratch testing with increasing fluoropolymer concentration. A progressively increasing load from 0.03 N to 12 N was administered with a diamond tip to the surfaces of the samples; depths were determined within ±7.5 nm. The original scratch depth is a function of the fluoropolymer concentration. Scratch recovery (healing) reaches values up to 95%. Plots of the residual depth versus concentration of the fluoropolymer at 4, 6, 8, and 10 N reveal minima for all forces and both temperatures. Addition of only 5% or 10% 12F-PEK improves the scratch recovery significantly. The results are explained by changes of material morphology with the fluoropolymer concentration.