Mechanism analysis and kinetic modeling of glycerol conversion into lactic acid in the alkaline media with and without heterogeneous catalyst Cu NPs are reported. The reaction pathways were determined in agreement with the experimental results and comprise several types of reactions, namely dehydrogenation, hydrogenolysis, dehydration and C–C cleavage. Experimental concentration-time profiles were obtained in a slurry batch reactor at different glycerol, NaOH and Cu NPs concentrations in a temperature range of 483–518 K. Power law, Langmuir–Hinshelwood (LH) and Eley–Rideal (ER) models were chosen to fit the experimental data. The proposed reaction pathways and obtained kinetic model adequately describe the experimental data. The reaction over Cu NPs catalyst in the presence of NaOH proceeds with a significantly lower activation barrier (E_a = 81.4 kJ∙mol⁻¹) compared with the only homogeneous catalytic conversion (E_a = 104.0 kJ∙mol⁻¹). The activation energy for glycerol hydrogenolysis into 1,2-propanediol on the catalyst surface without adding hydrogen is estimated of 102.0 kJ∙mol⁻¹. The model parameters obtained in this study would be used to scale an industrial unit in a reactor modeling.

In this review article, recent trends in the catalytic processes for the synthesis of lactic acid from glycerol are systematized. Based on literature data, the mechanisms of glycerol conversion in...

Copper (I, II) oxide powders were tested for glycerol conversion to lactic acid under alkaline conditions. Fresh and spent catalysts were characterized using powder X-ray diffraction, Scanning Electron Microscopy/Energy Dispersive X-ray Spectroscopy, the BET-nitrogen adsorption method and FTIR spectroscopy. In all cases, an almost complete in situ reduction of Cu (I, II) oxides into metallic Cu was observed, even after one catalytic run. Moreover, all the samples of spent catalysts showed similar catalytic activity regardless of their initial form and particle size. Commercial copper powders, prepared copper powders and in situ reduced copper catalysts were tested under the same conditions to compare their catalytic activity. It was shown that the in situ reduced copper catalyst had similar activity to the specially prepared copper powders and much higher activity compared to the commercial copper powders. The in situ reduced copper catalyst exhibited rather high stability. The glycerol conversion and lactic acid selectivity were about 98% and 70%, respectively, after ten catalytic cycles.