In this article, we have reported an environmentally benign and cost-effective method for the synthesis of monodispersed silver nanoparticles (AgNPs), based on Centella asiatica phenolic extracts (CAPE). The presence of phenolics was confirmed by ultra high-performance liquid chromatography coupled with electrospray ionization quadrupole time of flight mass spectrometry (UHPLC-ESI-qTOF-MS). Colloidal AgNPs synthesized under different concentrations of silver nitrate were monitored with a UV-vis spectrophotometer. Maximum absorption spectra intensity was found to range between 430–440 nm, during a synthesis time of 90 minutes at room temperature. The as-synthesized CAPE-AgNPs, was subjected to various instrumental characterizations such as, transmission electron microscopy (TEM), X-ray powder diffraction (XRD), energy dispersive X-ray spectroscopy (EDS), Fourier transform infrared (FTIR) spectroscopy, dynamic light scattering (DLS) and zeta potential. At the optimized synthesis conditions, spherical and monodispersed CAPE-AgNPs were obtained, with an absorption maximum at 430 nm. The crystalline CAPE-AgNPs had a face-centered-cubic (fcc) crystallographic structure, possessing average sizes estimated from TEM, to be between 20–25 nm diameter, a hydrodynamic diameter from DLS of about 90 nm and a zeta potential value of −28.7 mV. FTIR results validated the presence of phenolics on the surfaces of CAPE-AgNPs. The anti-microbial capacity of CAPE-AgNPs was further demonstrated on different pathogenic bacterial strains with satisfactory performances. As a result of the high surface area to volume ratio of CAPE-AgNPs, it was investigated as a catalyst towards the reduction of prominent environmental pollutants, 4 nitrophenol (4 NP), Congo red (CR) and methylene blue (MB). Pseudo first order kinetics were obtained with rate constants of 3.9 × 10⁻³ s⁻¹ for 4 NP, 54.7 × 10⁻³ min⁻¹ for MB and 5.6 × 10⁻³ s⁻¹ for CR. The catalytic performance and antimicrobial activities of CAPE-AgNPs suggest its potential application in wastewater treatment and control of pathogenic microbes.

Herein, the synthesis of a biocompatible silver nanoparticles (AgNPs), for colorimetric detection of toxic mercury (II) ion (Hg²⁺), is reported. Phenolic-rich fraction of Asystasia gangetica leaf was extracted and used as a reductant of silver salt, all within the hydrophilic konjac glucomannan (KgM) solution as stabilizer, at room temperature (RT). The bioactive components of Asystasia gangetica phenolic extract (AGPE), as elucidated with a (UHPLC-MS-QTOF-MS), revealed plethora of phenolic compounds, which can facilitate the reduction of silver salt at ambient conditions. Sparkling yellow colloidal solution of KgM-AgNPs was realized within 1 h, at RT, having a UV–vis maximum at 420 nm. KgM-AgNPs was characterized using UV–vis, Raman and (FTIR), TEM, SEM, EDS, XRD, TGA/DTG. TEM and FESEM images showed that KgM-AgNPs were spherical, with particle size distribution around 10–15 nm from TEM. The KgM-AgNPs biocompatibility was investigated on mouse L929 fibrobroblast and rat erythrocytes, without any harmful damages on the tested cells. In aqueous environment, KgM-AgNPs demonstrated good detection capacity toward Hg²⁺, in a Hg²⁺ concentration dependent fashion, within 3 min. Absorbance ratios (A₃₆₀/A₄₀₈) was linear with Hg²⁺ concentrations from 0.010–10.0 to 10.0–60.0 µM, with an estimated (LOD) of 3.25 nM. The probe was applied in lake water sample, with satisfactory accuracy.