Textile-reinforced concrete (TRC) has gained a lot of attraction in recent years. Adequate bond between the phases in this system allows to transfer high loadings, thus enabling high performance. The terminus textile reinforcement, however, comprises many different types of fabrics, which differ in their chemical composition, geometry, surface properties etc., and thus exhibit substantially different bond properties. In the course of RILEM’s Technical Committee 292 work on TRC it was found that a comprehensive understanding of the complex interactions between individual parameters is still lacking. This is amplified by the fact that different types of textile reinforcement are preferably used in different regions of the world. This paper therefore attempts to compile findings from literature on the bond in TRC. The database used was created in the course of the TC work. Additional papers of relevance were identified by scanning scientific web databases. The different influencing parameters are given in this paper in a hierarchical order, starting from the level of the individual constituents (filament and matrix) to impregnated fabrics and the influence of textile manufacturing and architecture on the bond. Finally, by mapping all the cited literature used in this paper based on grouped keywords the complex intercorrelations are visualised.

Steel structures are prone to corrosion, a chemical reaction between steel and the atmosphere that gradually weakens the material. Over time, this reaction can significantly reduce the structural integrity and lifespan of steel elements. Without intervention, corrosion can cause structures to fail, leading to financial, environmental, and potential human losses. Enhancing steel’s corrosion resistance is crucial, and one method involves adding niobium (Nb). Niobium microalloyed steels are known for their increased strength, and some research indicates that Nb may also improve corrosion resistance by making the grain structure of the steel finer. However, the complete potential of Nb in corrosion prevention remains underexplored, with significant research gaps across various scales, from microstructural impacts on durability to macroscopic effects on mechanical properties. The research community has utilized numerous experimental approaches to test corrosion resistance under different conditions, but there is a lack of comprehensive studies that aggregate and analyze these findings. This paper seeks to fill that void by reviewing the impact of Nb on the strength and corrosion resistance of structural steels, examining how steel beams’ ultimate capacity degrades over time and identifying key areas where further research is needed to understand Nb’s role in mitigating corrosion.