Infeed rotary swaging is a cold forming production technique to reduce the diameter of axisymmetric components. The forming is achieved discontinuously by a series of radial strokes that are spread over the shell of the part. Due to tolerances within the rotary swaging machine, these strokes perform individually and the resulting stroke pattern is not homogeneous with regards to circumferential and longitudinal distribution. Nevertheless, in combination with the high number of performed strokes and the large contact area between the dies and the part, the external part properties, such as diameter, roundness and surface roughness, show even values along the finished part. In contrast, strength-defining internal part properties, like microstructure and residual stress components, are more sensitive to the actual pattern and temporal sequence of the individual strokes, which is investigated in this study. The impact of process fluctuations during the conventional process, which are induced by the tolerances of machine tool components, was verified by numerical simulations, physical tests and measurements of residual stress distributions at the surface and at depth. Furthermore, a method is introduced to maintain the stroke following angle ∆φ at zero by flat dies, and thus the actual pattern and temporal sequence of the strokes was homogenized. The results show that the residual stress fluctuations at the surface could be controlled and reduced. Furthermore, it is demonstrated that the depth profile of the residual stresses at a distance of 300 µm from the surface developed independently from the process fluctuations.

Additionally to the achievable tight geometrical tolerances, rotary swaging can influence intrinsic material properties by work hardening and residual stresses generation. Although residual stresses should be usually avoided, they can be used on purpose to improve the performance properties of a produced part. To find prospective process settings, 2D FEM simulation of the rotary swaging process was developed and revealed the development of residual stresses distributions in E355 steel tubes in the whole longitudinal section. Besides the closing time, also geometric features of the dies were varied. It was found that the closing time affects the residual stresses significantly at the surface, but not in the depth of the part. By shortening the calibration zone, the axial tensile residual stresses near the outer surface could be lowered, while compressive residual stresses near the inner surface remained almost unaffected. By applying a higher die angle, the tensile axial residual stresses were increased while reducing the compressive axial residual stresses. Experimental investigations of residual stresses were performed by X-ray diffraction which revealed a good agreement between simulation results and physical measurements. With these findings, the rotary swaging process can be optimized for shaping residual stresses profiles to improve the performance properties of the produced parts.

Micro rotary swaging is a cold forming process for production of micro components with determined geometry and surface. It is also possible to change the microstructure of wires and hence the material properties. Swaging dies revolve around the work piece with an overlaid radial oscillation. Newly developed tools (Flat Surface Dies, FSD) feature plain surfaces and do not represent the geometry of the formed part as in conventional swaging. Using these tools allows for producing wires with triangle geometry (cross section) as well as a circular shape. To test the influence of FSD on material properties by micro swaging a new method is investigated: the variation of the relative speed between the specimen and dies in infeed rotary swaging. During this specific process copper (C11000) and steel (304 Alloy) wires with diameter d0 = 1 mm are formed. It is noticed that the mechanical characteristics such as ductility and strength differ from the characteristics after conventional swaging. Moreover this approach enables new possibilities to influence the geometry and the surface quality of wires. The impact of the relative speed on the processed wire features is described in this paper.

The radial infeed rotary swaging is widely used as a diameter reduction forming process of axisymmetric workpieces, improving the mechanical properties with excellent near net shape forming. In the present study, rotary swaging experiments with different parameter setups were performed on steel tubes and bars under different material states and several resulting property modifications were investigated such as stress-strain curve, hardness, fatigue strength and surface residual stresses. The results show a significant work hardening induced by the rotary swaging process and an improvement in the static and dynamic mechanical properties was observed. Furthermore, the hardness distribution was homogenous in the cross section of the rotary swaged workpieces. Moreover, depending on the process conditions, different residual stresses distribution were generated along the surface.

Rotary swaging is an incremental cold forming process that changes beneath the geometry also the microstructure and mechanical properties of the workpiece. Especially a new process design with Eccentric Flat Shaped Dies (EFSD) influences both the kind and amount of stress and plastic strain and consequently the material structure, and hence the material and workpiece properties. Eccentric rotary swaging typically provides a helical material flow. According to the process parameters the microstructure features a typical eddy pattern with a spiral shaped grain orientation. The forming process can be carried out in one or more process steps. In a multistage process, it is possible to change the feed direction and, hence, the material flow helix direction. This approach can be used as a possibility to improve the homogeneity of the workpiece and material properties. In addition, for this aims an intermediate heat treatment in multistage forming operations could be realized. Following the goal of optimizing the final properties, the question arises how these mechanical and thermal treatments affect the material microstructure and the forming properties of the workpiece and how they interact. Experiments were conducted with austenitic stainless steel rods of grade AISI304. The effects of the varied feed direction, feed velocity and heat treatment between the forming operations are discussed.

The projects of this chapter describe micro forming processes that are studied as single processes but can also be combined as process chains.