This study presents a novel method for the development of TiO₂/reduced graphene oxide (rGO) nanocomposites for photocatalytic degradation of dyes in an aqueous solution. The synergistic integration of rGO and TiO₂, through the formation of Ti–O–C bonds, offers an interesting opportunity to design photocatalyst nanocomposite materials with the maximum absorption shift to the visible region of the spectra, where photodegradation can be activated not only with UV but also with the visible part of natural solar irradiation. TiO₂@rGO nanocomposites with different content of rGO have been self-assembled by the hydrothermal method followed by calcination treatment. The morphological and structural analysis of the synthesized photocatalysts was performed by FTIR, XRD, XPS, UV-Vis DRS, SEM/EDX, and Raman spectroscopy. The effectiveness of the synthesized nanocomposites as photocatalysts was examined through the photodegradation of methylene blue (MB) and rhodamine B (RhB) dye under artificial solar-like radiation. The influence of rGO concentration (5 and 15 wt.%) on TiO₂ performance for photodegradation of the different dyes was monitored by UV-Vis spectroscopy. The obtained results showed that the synthesized TiO₂@rGO nanocomposites significantly increased the decomposition of RhB and MB compared to the synthesized TiO₂ photocatalyst. Furthermore, TiO₂@rGO nanocomposite with high contents of rGO (15 wt.%) presented an improved performance in photodegradation of MB (98.1%) and RhB (99.8%) after 120 min of exposition to solar-like radiation. These results could be mainly attributed to the decrease of the bandgap of synthesized TiO₂@rGO nanocomposites with the increased contents of rGO. Energy gap (E_g) values of nanocomposites are 2.71 eV and 3.03 eV, when pure TiO₂ particles have 3.15 eV. These results show the potential of graphene-based TiO₂ nanocomposite to be explored as a highly efficient solar light-driven photocatalyst for water purification.

Alumina (Al₂O₃) and zirconia (ZrO₂) have good overall properties and thus are widely used oxide technical ceramics. The biggest drawback of Al₂O₃ is its low fracture toughness. In contrast, ZrO₂ is relatively tough, but is also much more expensive. In order to improve the alumina toughness, composite ceramics are being developed. Slip casting technology has economic advantages over the conventional hot isostatic pressure technology, but problems may arise when preparing stable highly-concentrated suspensions (slip) for filling the mold. The purpose of this study is to prepare aqueous suspensions using 70 wt. % α-Al₂O₃, with 0, 1, 5 and 10 wt. % of added t-ZrO₂. Suspensions were electrosterically stabilized using the ammonium salt of polymethylacrylic acid, an alkali-free anionic polyelectrolyte dispersant. Also, magnesium oxide in form of magnesium aluminate spinel (MgAl₂O₄) was used to inhibit the abnormal alumina grain growth during the sintering process. Minimum viscosities were used as stability estimators, where an increase in ZrO₂ content required adding more dispersant. After sintering, the Vickers indentation test was used to determine the hardness and the indentation fracture toughness from the measurement of the crack length. Also, the brittleness index (B_i, μm^−1/2) was calculated from values of Vickers hardness and the Vickers indentation fracture toughness. It was found that with increasing ZrO₂ content the fracture toughness increased, while the hardness as well as the brittleness index decreased. Zirconia loading reduces the crystallite sizes of alumina, as confirmed by the X-ray diffraction analysis. SEM/EDS analysis showed that ZrO₂ grains are distributed in the Al₂O₃ matrix, forming some agglomerates of ZrO₂ and some pores, with ZrO₂ having a smaller grain size than Al₂O₃.