The early-age hydration processes of concretes with mineral admixtures have been monitored and evaluated by a newly developed ultrasonic method based on embedded cement-based piezoelectric composite sensors. With the embedded ultrasonic (P-wave) measurement system, the waveform, wave velocity, attenuation coefficient index, and frequency-domain spectrum of detected ultrasonic waves during hydration can be recorded. The mineral admixtures examined include fly ash, slag, and silica fume, which replace part of the cement in concrete mixtures. It is found that the ultrasonic transmission parameters can be related to the microstructure changes of the concrete. Both the acceleration effects of silica fume and the retardation effects of fly ash and slag on the early hydration of concrete can be determined and explained through the analysis and comparison of the characteristics of the velocity curves. The attenuation coefficient index curve provides additional observation for the study of hydration kinetics. Moreover, the function of fresh concrete in filtering the high-frequency component of the wave varies with time, and concrete can be considered as low-pass frequency spectral filter. Frequency spectra analysis at different ages of fresh concrete provides useful information to reveal the early-age hydration process.

Backscattered electron (BSE) imaging has been widely used to investigate the microstructure of cement-based materials, and it has shown specific advantages in determining the fractions and distribution of individual phases. The lower and upper grey level thresholds for the investigated phases need to be determined as the key references for BSE image analysis. However, the traditional determination of the grey level thresholds for phases is quite arbitrary. A novel method is proposed to analyse BSE images of cement-based materials using statistical analysis, avoiding the subjective choice of grey level thresholds.

In this paper, concrete specimens are immersed in ultrapure water, to study the evolutions of surface permeability, pore structure and paste microstructure following the prolonging of immersion period. According to the results, after 30-day immersion, the surface permeability of concrete becomes higher as compared with the value before immersion. However, further immersion makes the surface permeability decrease, so that the value measured after 150-day immersion is only half that measured after 30-day immersion. The early increase in surface permeability should be mainly attributed to the leaching of calcium hydroxide, while the later decrease to the refinement of pore structure due to hydration. The two effects work simultaneously and compete throughout the immersion period. The proposed mechanisms get support from microscopic measurements and observations.