MoS₂/RGO composite hollow microspheres were hydrothermally synthesized by using SiO₂/GO microspheres as a template, which were obtained via the sonication-assisted interfacial self-assembly of tiny GO sheets on positively charged SiO₂ microspheres. The structure, morphology, phase, and chemical composition of MoS₂/RGO hollow microspheres were systematically investigated by a series of techniques such as FE-SEM, TEM, XRD, TGA, BET, and Raman characterizations, meanwhile, their electrochemical properties were carefully evaluated by CV, GCD, and EIS measurements. It was found that MoS₂/RGO hollow microspheres possessed unique porous hollow architecture with high-level hierarchy and large specific surface area up to 63.7 m²·g⁻¹. When used as supercapacitor electrode material, MoS₂/RGO hollow microspheres delivered a maximum specific capacitance of 218.1 F·g⁻¹ at the current density of 1 A·g⁻¹, which was much higher than that of contrastive bare MoS₂ microspheres developed in the present work and most of other reported MoS₂-based materials. The enhancement of supercapacitive behaviors of MoS₂/RGO hollow microspheres was likely due to the improved conductivity together with their distinct structure and morphology, which not only promoted the charge transport but also facilitated the electrolyte diffusion. Moreover, MoS₂/RGO hollow microsphere electrode displayed satisfactory long-term stability with 91.8% retention of the initial capacitance after 1000 charge/discharge cycles at the current density of 3 A·g⁻¹, showing excellent application potential.

We report the synthesis of nitrogen-doped hierarchical meso/microporous carbon using renewable biomass bamboo fungus as precursor via two-step pyrolysis processes. It is found that the developed porous carbon (NHPC-800) features honeycomb-like cellular framework with well-developed porosity, huge specific surface area (1708 m² g⁻¹), appropriate nitrogen-doping level (3.2 at.%) and high mesopore percentage (25.5%), which are responsible for its remarkable supercapacitive performances. Electrochemical tests suggest that the NHPC-800 electrode offers the largest specific capacitance of 228 F g⁻¹, asplendid rate capability and stable electrochemical behaviors in a traditional three-electrode system. Additionally, asymmetric supercapacitor device is built based on this product as well. An individual as-assembled supercapacitor of NHPC-800//NHPC-800 delivers the maximum energy density of 4.3 Wh kg⁻¹; retains the majority of capacitanceat large current densities; and shows terrific cycling durability with negligible capacitance drop after long-term charge/discharge for beyond 10,000 cycles even at a high current density of 10 A g⁻¹. These excellent supercapacitive properties of NHPC-800 in both three- and two-electrode setups outperform those of lots of biomass-derived porous carbons and thus make it a perspective candidate for producing cost-effective and high-performance supercapacitors

Using graphene oxide as substrate and stabilizer for the silver nanoparticles, silver nanoparticles-graphene oxide (Ag NPs/GO) composites with different Ag loading were synthesized through a facile solution-phase method. During the synthesis process, AgNO₃on GO matrix was directly reduced by NaBH₄. The structure characterization was studied through X-ray diffraction (XRD), atomic force microscopy (AFM), high-resolution transmission electron microscope (HRTEM), ultraviolet-visible spectroscopy (UV-Vis), and selected area electron diffraction (SAED). The results show that Ag nanoparticles (Ag NPs) with the sizes ranging from 5 to 20 nm are highly dispersed on the surfaces of GO sheets. The shape and size of the Ag NPs are decided by the volume of initial AgNO₃solution added in the GO. The antibacterial activities of Ag NPs/GO nanocomposites were investigated and the result shows that all the produced composites exhibit good antibacterial activities against Gram-negative (G−) bacterial strainEscherichia coli(E. coli) and Gram-positive (G+) strainStaphylococcus aureus(S. aureus). Moreover, the antibacterial activities of Ag NPs/GO nanocomposites gradually increased with the increasing of volume of initial AgNO₃solution added in the GO and this improvement of the antibacterial activities results from the combined action of size effect and concentration effect of Ag NPs in Ag NPs/GO nanocomposites.

Hierarchical micro-mesoporous carbon (denoted as HPC-2 in this study) was synthesized by pre-carbonization of biomass Sichuan pepper followed by KOH activation. It possessed well-developed porosity with the specific surface area of 1823.1 m² g⁻¹ and pore volume of 0.906 cm³ g⁻¹, and exhibited impressive supercapacitive behaviors. For example, the largest specific capacitance of HPC-2 was tested to be ca. 171 F g⁻¹ in a three-electrode setup with outstanding rate capability and stable electrochemical property, whose capacitance retention was near 100% after cycling at rather a high current density of 40 A g⁻¹ for up to 10,000 cycles. Furthermore, a two-electrode symmetric supercapacitor cell of HPC-2//HPC-2 was constructed, which delivered the maximum specific capacitance and energy density of ca. 30 F g⁻¹ and 4.2 Wh kg⁻¹, respectively, had prominent rate performance and cycling stability with negligible capacitance decay after repetitive charge/discharge at a high current density of 10 A g⁻¹ for over 10,000 cycles. Such electrochemical properties of HPC-2 in both three- and two-electrode systems are superior or comparable to those of a great number of porous biomass carbon reported previously, hence making it a promising candidate for the development of high-performance energy storage devices.

In this study, we report on the rational design and facile preparation of a cotton-reduced graphene oxide-silver nanoparticle (cotton-RGO-AgNP) hybrid fiber as an electrode for the building of a flexible fiber-shaped supercapacitor (FSSC). It was adequately characterized and found to possess a well-defined core−shell structure with cotton yarn as a core and a porous RGO-AgNP coating as a shell. Thanks to the unique morphological features and low electrical resistance (only 2.3 Ω·cm⁻¹), it displayed attractive supercapacitive properties. When evaluated in a three-electrode setup, this FSSC electrode delivered the highest linear and volumetric specific capacitance of up to ca. 12.09 mF·cm⁻¹ and ca. 9.67 F·cm⁻³ with a satisfactory rate capability as well as a decent cycling stability. On the other hand, an individual parallel symmetric FSSC cell constructed by this composite fiber fulfilled the largest linear and volumetric specific capacitance of ca. 1.67 mF·cm⁻¹ and ca. 0.67 F·cm⁻³ and offered the maximum energy density, as high as ca. 93.1 μWh·cm⁻³, which outperformed a great number of graphene- and textile yarn-based FSSCs. Impressively, bending deformation brought about quite a limited effect on its electrochemical behaviors and almost no capacitance degradation took place during the consecutive charge/discharge test for over 10,000 cycles. Consequently, these remarkable performances suggest that the currently developed cotton-RGO-AgNP fiber has considerable application potential in flexible, portable and wearable electronics.