An excellent transparent film with effective absorption property in near-infrared (NIR) region based on cesium-doped tungsten oxide nanoparticles was fabricated using a facile double layer coating method via the theoretical considerations. The optical performance was evaluated; the double layer-coated film exhibited 10% transmittance at 1,000 nm in the NIR region and over 80% transmittance at 550 nm in the visible region. To optimize the selectivity, the optical spectrum of this film was correlated with a theoretical model by combining the contributions of the Mie-Gans absorption-based localized surface plasmon resonance and reflections by the interfaces of the heterogeneous layers and the nanoparticles in the film. Through comparison of the composite and double layer coating method, the difference of the nanoscale distances between nanoparticles in each layer was significantly revealed. It is worth noting that the nanodistance between the nanoparticles decreased in the double layer film, which enhanced the optical properties of the film, yielding a haze value of 1% or less without any additional process. These results are very attractive for the nanocomposite coating process, which would lead to industrial fields of NIR shielding and thermo-medical applications. 78.67.Sc; 78.67.Bf; 81.15.-z

EPOSS of polyhedral oligomeric silsesquioxanes (POSS) mixture structure and LPSQ of ladder-like polysilsesquioxane (LPSQ) structure were synthesized via sol–gel reaction. EPSQ had a high molecular weight due to polycondensation by potassium carbonate. The EPSQ film showed uniform surface morphology due to regular double-stranded structure. In contrast, the EPOSS-coated film showed nonuniform surface morphology due to strong aggregation. Due to the aggregation, the EPOSS film had shorter d-spacing (d1) than the EPSQ film in XRD analysis. In pencil hardness and nanoindentation analysis, EPSQ film showed higher hardness than the EPOSS film due to regular double-stranded structure. In addition, in the in-folding (r = 0.5 mm) and out-folding (r = 5 mm) tests, the EPSQ film did not crack unlike the EPOSS coated film.

In this study, novel silane acrylates, such as diethylene glycol diacrylate (DEGDA) and tetraethylene glycol diacrylate (TEGDA), containing ethylene glycol chains were synthesized and introduced into acrylic pressure-sensitive adhesives (PSAs) to regulate their peel strength and rheological properties. The synthesized silane acrylates effectively improved the cohesion and adhesive properties of the acrylic PSAs, even with only 1 wt% addition. In addition, the glass transition temperature and flexibility of acrylic PSAs were also affected by the increase in free volume induced by ethylene glycol chains. The silane acrylates also improved the viscoelasticity of the acrylic PSAs, which exhibited excellent recovery (62–96%) and stress relaxation (>90%) properties owing to the increased elasticity. Additionally, the acrylic PSAs prepared with the silane acrylates showed excellent optical properties (transmittance ≥ 90%, haze ≤ 1%) and exhibited behavior suitable for application in flexible displays from a comprehensive perspective.

Research studies based on flexible organic electronic devices regarding the relationship between carrier transport and molecular stacking are actively reported. For enhancing carrier transport and mechanical strength, new types of anthracene derivatives (ANT), exhibiting parallel dominant molecular stacking characteristics, are designed and synthesized. They show parallel dominant molecular stacking properties inducing excellent carrier transport through hybridization with perpendicular materials. They are introduced as electron transport layers (ETLs) for organic solar cells (OSCs), organic light emitting diodes (OLEDs), and organic nano-generators (ONGs). Hybrid ETLs show excellent carrier transport characteristics, exhibiting minimized energy loss and suppressed carrier recombination resulting from relative resonance through partial polarization of ANT. Consequently, the power conversion efficiency (PCE) of the fabricated OSCs based on fullerene and non-fullerene systems reaches 9.6% and 11.4%, and the luminescence of OLEDs reaches up to 17 057 cd m⁻². In addition, flexible OSCs, OLEDs, and ONGs show improved output performance and mechanical strength due to excellent carrier transport. Especially, in flexible ONGs, high carrier transport can be helpful for enhancing output voltage by energy level shifting.