Chromium is a toxic and carcinogenic heavy metal that originates from various human activities. Therefore, the effective removal of chromium from aqueous solutions is an extremely important global challenge. Herein, we report a chitosan-coated iron oxide nanoparticle immobilized hydrophilic poly(vinylidene) fluoride membrane (Chi@Fe₂O₃–PVDF) which can potentially be used for efficient removal of hexavalent chromium(VI) by a simple filtration process. Membrane filtration is an easy and efficient method for treating large volumes of water in a short duration. The adsorption experiments were conducted by batch and continuous in-flow systems. The experimental data showed rapid capture of hexavalent chromium (Cr(VI)) which can be explained by the pseudo-second-order kinetic and Langmuir isotherm model. The nanocomposite membrane exhibited high adsorption capacity for Cr(VI) (14.451 mg/g in batch system, 14.104 mg/g in continuous in-flow system). Moreover, its removal efficiency was not changed significantly in the presence of several competing ions, i.e., Cl⁻, NO₃⁻, SO₄²⁻, and PO₄³⁻. Consequently, the Chi@Fe₂O₃-PVDF-based filtration process is expected to show a promising direction and be developed as a practical method for wastewater treatment.

Anionic dyes are one of the most serious contaminants in water as these molecules are known to be toxic to many living organisms. Herein, we report the development of functionalized polyvinylidene fluoride membranes modified with chitosan-coated iron oxide nanomaterials (Fe-PVDF) for the efficient treatment of anionic dye-contaminated water. Aqueous solutions of anionic dyes could be captured rapidly by passing through the functionalized membrane under reduced pressure. Under neutral conditions, Fe-PVDF showed a maximum removal capacity of 74.6 mg/g for Evans blue (EB) through the adsorption process. In addition, the adsorption capacity was significantly enhanced up to 434.78 mg/g under acidic conditions. The adsorption process for EB matched well with the Langmuir model, indicating monolayer adsorption of the dye to the membrane surface. Moreover, Fe-PVDF can be reusable by a simple washing step in an alkaline solution, and thus, the composite membrane was applied several times without a significant decrease in its adsorption performance. The same composite membrane was further applied to the removal of five other different anionic dyes with high efficiencies. The adsorption mechanism can be explained by the electrostatic interaction between the positively charged chitosan and the negatively charged dye as well as the affinity of the sulfate groups in dye molecules for the surface of the iron oxide nanoparticles. The easy preparation and rapid decolorization procedures make this composite membrane suitable for efficient water treatment.

A Zn(II)-based metal–organic framework (MOF) compound and MnO₂ were used to prepare ZnO_x[email protected]₂ composites for selective Sr²⁺ removal in aqueous solutions. The ZnO_x[email protected]₂ composites were characterized by Fourier transform infrared spectroscopy, scanning electron microscopy, thermogravimetric analysis, and Brunauer–Emmett–Teller surface area analysis. The functional groups, morphologies, thermal stabilities, and specific surface areas of the composites were suitable for Sr²⁺ adsorption. A maximum adsorption capacity of 147.094 mg g^–1 was observed in batch adsorption experiments, and the sorption isotherms were fit well by the Freundlich model of multilayer adsorption. Adsorption reached equilibrium rapidly in kinetic experiments and followed the pseudo-second-order kinetic model. The adsorption capacity of the ZnO_x[email protected]₂ composite with the highest MnO₂ content was high over a wide pH range, and the composite was highly selective toward Sr²⁺ in solutions containing coexisting competing ions. Also, it has a good reusability for removing Sr²⁺.