Transparent wood samples were fabricated from an environmentally-friendly hydrogen peroxide (H₂O₂) bleached basswood (Tilia) template using polymer impregnation. The wood samples were bleached separately for 30, 60, 90, 120 and 150 min to evaluate the effects on the changes of the chemical composition and properties of finished transparent wood. Experimental results showed decreases in cellulose, hemicellulose, and lignin content with an increasing bleaching time and while decreasing each component to a unique extent. Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscope (SEM) analysis indicated that the wood cell micro-structures were maintained during H₂O₂ bleaching treatment. This allowed for successful impregnation of polymer into the bleached wood template and strong transparent wood products. The transparent wood possessed a maximum optical transmittance up to 44% at 800 nm with 150 min bleaching time. Moreover, the transparent wood displayed a maximum tensile strength up to 165.1 ± 1.5 MPa with 90 min bleaching time. The elastic modulus (E_r) and hardness (H) of the transparent wood samples were lowered along with the increase of H₂O₂ bleaching treatment time. In addition, the transparent wood with 30 min bleaching time exhibited the highest E_r and H values of 20.4 GPa and 0.45 GPa, respectively. This findings may provide one way to choose optimum degrees of H₂O₂ bleaching treatment for transparent wood fabrication, to fit the physicochemical properties of finished transparent wood.

Transparent wood (TW) was prepared by directly impregnating the wood cell wall and cavity with index-matched prepolymerized methyl methacrylate (MMA). In this process, lignin is retained compared with the preparation of transparent wood in the past, making the production faster and more energy-efficient. The innovation lies in that the prepared transparent wood retains the natural color and texture of the wood while transmitting light, especially under the illumination of a specific light source, which exist as the special visual effects. In order to enhance the practicality of the research and effectively expand the types of home decoration materials, six common wood species with different densities were selected in the experiment. Then the characteristics and mechanisms of wood, that is, color difference, light transmittance, microstructure, changes of chemical functional groups, and tensile strength, before and after PMMA impregnating were compared and analyzed. It is concluded that the light transmittance and mechanical properties of the wood have been improved, and a good synergistic effect between wood and PMMA has been confirmed by the analysis of scanning electron microscopy and infrared spectroscopy. The above highlights make pervious to transparent wood, which has the potential as an excellent functional decorative material.

The excellent oil absorption capacity and sustainability advantages of adsorbent-type oil-absorbing products have become the primary method to deal with marine oil spills and organic pollution at this stage, especially aerogel products. However, this type of material also has some problems, such as secondary pollution during nanocellulose preparation. Lignin and hemicellulose were removed from the natural wood, and followed by the action of freeze drying, the wood sponge was prepared. Then, followed by immersing the wood sponge into polyvinyl alcohol solution (PVA) and dipping it in polydimethylsiloxane solution, the target PVA-reinforced wood sponge with better mechanical compressibility and hydrophobic properties was obtained. The new wood sponge showed high mechanical compressibility (reversible compression rate of 40%) and elastic recovery rate (the height retention rate was about 100% after 200 cycles of 30% strain). It also showed excellent hydrophobic and oleophilic properties, and the water contact angle was up to 138°, and the oil absorption capacity was 25 g·g^–1. The ability of oil absorption can be recovered by compression, and the high absorption rate was maintained after 50 cycles. The wood sponge has great potential in reusable oil–water separation due to low cost, high efficiency, high performance, biodegradability, environmental friendliness, and other advantages.

In this paper, Moso bamboo (Phyllostachys heterocycle) before and after heat treatment were used as raw materials to prepare transparent bamboo (TB). In an acidic environment, the lignin contained in the bamboo material was removed to obtain a bamboo template, and an epoxy resin similar to the cellulose refractive index was used for vacuum impregnation into the bamboo template to obtain a transparent bamboo material. The purpose of this study was to compare the physical and chemical properties of TB and original bamboo and the differences between TBs before and after heat treatment, taken from different parts of bamboo, in order to explore the performance advantages and disadvantages of TB as a new material. The Fourier transform infrared spectroscopy analysis (FTIR), scanning electron microscope testing (SEM), three elements analysis, light transmittance testing, and mechanical strength testing were used to study the molecular composition, microstructure, chemical composition, light transmittance, and tensile strength of the TB samples. The results showed that the lignin content of the delignified bamboo templates was greatly reduced. In addition, the SEM images showed that a large amount of epoxy resin (type E51 and type B210 curing agent) was covered on the cross-section surface and pores of the TB samples. The FTIR showed that the epoxy molecular groups appeared on the TB, and the delignified bamboo template and the resin had a good synergy effect. According to the light transmittance testing, the original bamboo samples hardly contained light transmittance under visible light. The transmittance of transparent inner bamboo (TIB) and transparent heat-treated inner bamboo (THIB) could reach about 11%, and the transmittance of transparent outer bamboo (TOB) and transparent heat-treated outer bamboo (THOB) was about 2%. The light transmittance had been significantly improved when compared with the original bamboo samples. The transmittances of the TB samples before and after heat treatment in different parts of bamboo were different. In the visible light irradiation range, the light transmittances of TB samples were as follows: TIB > THIB and THOB > TOB. Meanwhile, the tensile strength of TB was reduced, especially for TOB and THOB. In addition, TB has a wide range of raw materials, and the preparation process is environmentally friendly. It can be used for decorative materials in homes, buildings, etc., and has a great application potential.