Background and methods: In this study, gelatin was blended with polyglycolic acid (PGA) at different ratios (0, 10, 30, and 50 wt%) and electrospun. The morphology and structure of the scaffolds were characterized by scanning electron microscopy, Fourier transform infrared spectroscopy, and differential scanning calorimetry. The mechanical properties were also measured by the tensile test. Furthermore, for biocompatibility assessment, human umbilical vein endothelial cells and human umbilical artery smooth muscle cells were cultured on these scaffolds, and cell attachment and viability were evaluated. Results: PGA with 10 wt% gelatin enhanced the endothelial cells whilst PGA with 30 wt% gelatin increased smooth muscle cell adhesion, penetration, and viability compared with the other scaffold blends. Additionally, with the increase in gelatin content, the mechanical properties of the scaffolds were improved due to interaction between PGA and gelatin, as revealed by Fourier transform infrared spectroscopy and differential scanning calorimetry. Conclusion: Incorporation of gelatin improves the biological and mechanical properties of PGA, making promising scaffolds for vascular tissue engineering.

As medical research progresses, the derivation and development of biological materials such as hydrogels have steadily gained more interest. The biocompatibility and non-toxicity of chitosan make chitosan hydrogels potential carriers for drug delivery. This work aims to develop two multi-reactive, safe, and highly swellable bio-hydrogels consisting of chitosan-graft-glycerol (CS-g-gly) and carboxymethyl chitosan-graft-glycerol (CMCS-g-gly), for sustained and controlled drug release, improved bioavailability along with entrapment in nanocarriers, which reduces side effects of vincristine sulphate. CS-g-gly and CMCS-g-gly are successfully prepared and fully characterized using analytical techniques. Under various conditions, the prepared hydrogels exhibit a high swelling ratio. Vincristine-loaded CS-g-gly (VCR/CS-g-gly), and CMCS-g-gly (VCR/CMCS-g-gly) show high encapsulation efficiency between 72.28-89.97%, and 56.97-71.91%, respectively. VCR/CS-g-gly show a sustained release behavior, and the maximum release of VCR from hydrogels reached 82% after 120 h of incubation. MCF-7 (breast cancer cell line) and MCF-10 (normal breast cell line) are evaluated for cell viability and apoptosis induction. The in-vitro anti-tumor efficacy is investigated using flow cytometry. The tetrazolium-based MTT assay of hydrogels shows no evidence of significant cytotoxicity in MCF-7 and MCF-10 cells. According to these findings, these hydrogels can effectively deliver drugs to MCF-7 and other breast cancer cells.