For truss structures, the question of whether to weld hidden welds or not has been controversial. In the actual construction process of truss structures, the members are usually spot welded in place on the assembly platform, and then welded as a whole, while the hidden welds of the truss are not welded, especially for small pipe diameter trusses. Furthermore, in this study, under hidden weld unwelded conditions, two kinds of reinforcing method (adding a half outer sleeve on each joint and filling concrete into the chord members) are adopted to achieve the purpose of strengthening the truss. Therefore, this paper presents an experimental study on the static behavior of four types of Warren tubular trusses made of CHS members. These four types are (1) T-HW: The truss with hidden welds welded; (2) T-HN: The truss with hidden welds unwelded; (3) TS-AS: The truss strengthened on the basis of T-HN by adding a half outer sleeve on each joint; (4) TS-FC: The truss strengthened on the basis of T-HN by filling concrete into the top and bottom chord members. The mechanical behavior, failure mode, bearing capacity, and load-displacement of all specimens were investigated. The surface plasticity of the bottom chord member, the weld fracture around tubular joints at the bottom chord member, and the bending deformation of the bottom chord member were observed in the tests. Compared with the T-HW specimen, the load carrying capacity of the T-HN specimen decreased by 18%. On the other hand, the T-HN specimen has better deformability than the T-HW specimen. The reinforcing method of adding a half outer sleeve on each joint and filling concrete into the chord members can effectively improve the load carrying capacity and stiffness of the truss, thus reducing the overall deformation of the truss, but the reinforcing method of filling concrete into the chord members is more efficient.

Due to the insufficient radial stiffness of the steel tube, the cracking of the weld and the plastic deformation of the string often occur under the cyclic loading of the hollow section pipe joint. In order to avoid such a failure, the overlapped K-joints were strengthened by pouring different concrete into the chords. Furthermore, to explore the detailed effect of filling different concrete in a chord on the hysteretic behavior of the overlapped K-joints, six full-scale specimens were fabricated by two forms, which included the circular chord and braces, the square chord and circular braces, and the low cyclic loading tests, which were carried out. The failure modes, hysteretic curves and skeleton curves of the joints were obtained, and the bearing capacity, ductility and energy dissipation of the joints were evaluated quantitatively. The results showed that plastic failure occurs on the surface of the chord of the joints without filling concrete, while the failure mode of the joints filled with concrete in the chords was the tensile failure of the chords at the weld of the brace toe, and the compressive braces had a certain buckling deformation; The strengthening measures of concrete filled with chord can effectively improve the mechanical properties of the K-joints, the delay of the plastic deformation of the chord, and improve the bearing capacity of the K-joints. Contrarily, the ductility coefficient and the energy dissipation ratio of K-joints decreased with the concrete filled in the chord. The hysteretic behavior of the K-joints with a circular chord and brace was slightly better than that of the K-joints with a square chord and circular brace, and the hysteretic behavior of the K-joints strengthened with fly ash concrete, which was better than that of the K-joints strengthened with ordinary concrete. The results of ANSYS (a large general finite element analysis software developed by ANSYS Company in the United States) analysis agreed well with the experimental results.