We study the conformations of polymer chains in polymer–graphene oxide nanocomposites. We show that the chains have a reduced radius of gyration that is consistent with confinement at a solid interface in the melt, as is expected for well-dispersed, high aspect ratio nanoparticles that are much larger than the polymer coil size. We show that confinement of the polymer chains causes a corresponding reduction in interchain entanglements, and we calculate a contribution to the plateau modulus from the distorted polymer network via a simple scaling argument. Our results are a significant step forward in understanding how two-dimensional nanoparticles affect global material properties at low loadings.

Nanocrystal quantum dots are generally coated with an organic ligand layer. These layers are a necessary consequence of their chemical synthesis, and in addition they play a key role in controlling the optical and electronic properties of the system. Here we describe a method for quantitative measurement of the ligand layer in 3 nm diameter lead sulfide–oleic acid quantum dots. Complementary small-angle X-ray and neutron scattering (SAXS and SANS) studies give a complete and quantitative picture of the nanoparticle structure. We find greater-than-monolayer coverage of oleic acid and a significant proportion of ligand remaining in solution, and we demonstrate reversible thermal cycling of the oleic acid coverage. We outline the effectiveness of simple purification procedures with applications in preparing dots for efficient ligand exchange. Our method is transferrable to a wide range of colloidal nanocrystals and ligand chemistries, providing the quantitative means to enable the rational design of ligand-exchange procedures.